Abstract:Solidification of the aluminum alloys takes place in heat-resistant refractory materials made of either metal or oxides that are stable at high temperatures. The significantly different thermal conductivities between metals and heat-resistant oxides cause solidification with significantly different cooling rates. In this work, we formed a secondary Al-8wt%Si-3wt%Cu alloy in a stainless steel mould, a thin-walled stainless steel cup, and a thick-walled zirconium oxide cup. The course of the formation of the solidified structure was monitored by immersed thermocouples, which enabled the computer analysis of the cooling curves. The parameters on which the cooling rate had the most significant influence are the undercooling values of the formation of primary aluminum crystals, the time of the growth of primary aluminum crystals and the total solidification time from the formation of the first solid crystals to the formation of a fully solidified structure. The Al-8wt%Si-3wt%Cu aluminum alloy formed in metal mould has a smaller grain size and consequently higher tensile strength, lower macro-porosity and less rough surface than the alloy formed in refractory oxide coatings. The examined heat-resistant refractory material influenced the formation of three basic micro-constituents in the Al-8wt%Si-3wt%Cu alloy in different time intervals, which led to the formation of a different microstructure, where the decision on the choice of material for the heat-resistant refractory material depends on the profitability of the entire process, the required quality of the external surfaces and required minimum strength of the final product.

Effect of Processing Parameters on Microstructure in Brazing of Al–Si Alloys

Phase Transformations under Heat Treatment of Al – Si + Flux Composite Brazing Metal

Microstructures Characteristics and Properties of Solidified Aluminum Alloy Brazed Joint

Effect of Strontium and SmO on the Microstructure and Fracture Mode of AlSi-Mg2Si Brazing Filler Metal

Effects of processing parameters on microstructure and mechanical behavior of SiO2/Ti–6Al–4V joint brazed with AgCu/Ni interlayer

Interfacial Microstructure and Forming Mechanism of Brazing Cf/Al Composite with Al–Si Filler

Investigation on microstructure and its transformation mechanisms of B2O3-SiO2-Al2O3-CaO brazing flux system

Effect of ultrasonic melt processing and Al-Ti-B on the microstructural refinement of recycled Al alloys

Dendritic growth in Al–Si alloys during brazing. Part 2: Computational modeling

Influence of Processing Parameters on the Microstructure of (aln+mg2si)/mg Metal Matrix Composites

Metallurgical interactions in solid/liquid diffusion couples of AA4343/AA3xxx/AA4343 layered aluminum sheet

Effect of Brazing Parameters on Microstructure and Mechanical Properties of Ti5Si3/Ti3Al Composite Joints Brazed with Ti–Zr–Cu–Ni Filler Alloy

The effect of the refractory material on the phase transformation parameteres during forming of the Al-8wt%Si-3wt%Cu structure

Effect of Brazing Temperature on Microstructure and Mechanical Properties of TiAl/ZrB2 Joint Brazed with CuTiZrNi Filler

Microstructure and mechanical response of the SiO2f/SiO2 composite and Invar alloy joints brazed with an AgCuTi alloy

Dendritic Growth in Al–Si Alloys During Brazing. Part 1: Experimental Evidence and Kinetics

Effect of process conditions on the evolution of microstructure and mechanical properties of AA3003 vacuum furnace brazing joints

Microstructure and properties of joint for stirring brazing of dissimilar Al/Mg alloy during heating processes

Effects of Solidification Thermal Variables on the Microstructure and Hardness of the Silicon Aluminum Bronze Alloy CuAl6Si2

Processing, microstructure and mechanical properties of vacuum-brazed Al 2O 3/Ti6Al4V joints

Effects of Glass Composition and Joining Parameters on Microstructural Evolution and Mechanical Properties of Al2O3/Cu Joints Brazed with Bi2O3-B2O3-ZnO Glass