Brazing of Transparent Polycrystalline Al2O3 and GH99 with the Assistance of (cu, Ni) Solid Solution Cladding Layer

Bo Zhang,Lixia Zhang,Sun Zhan,Jicai Feng

DOI: https://doi.org/10.21203/rs.3.rs-18928/v1

2020-01-01

Abstract:In this study, pure Cu foil was firstly vacuum cladding on the GH99 alloy (GH99) surface to prepare a (Cu, Ni) solid solution layer. By varying the cladding temperatures, (Cu, Ni) solid solution layers with different Ni contents were achieved. The vacuum cladding process was then followed by vacuum brazing of the Cu-coated GH99 to transparent polycrystalline Al 2 O 3 (TPA). Typical microstructure of the TPA/Cu-cladding GH99 brazed joint was characterized. The effects of different cladding temperatures on microstructural evolution and mechanical response of the brazed joints were discussed. By varying the cladding temperature, different thickness of the reaction layer at the braze filler/TPA interfaces can be achieved, which shows a strong correlation with the mechanical performance of the brazed joint. The maximum shear strength of the brazed joint reached 103 MPa when the cladding temperature was 1105 ºC. Compared with the directly brazed joint, shear strength was improved by 472%.