A Method To Extract The Intrinsic Mechanical Properties Of Soft Metallic Thin Films Based On Nanoindentation Continuous Stiffness Measurement Technique
X. Y. Zhou,Z. D. Jiang,H. R. Wang,Q. Zhu
DOI: https://doi.org/10.1088/1742-6596/48/1/204
2006-01-01
Abstract:In order to determine accurately the intrinsic hardness of the soft metallic thin film on a hard substrate using nanoindentation, a proper methodology irrespective of several important effects the Oliver-Pharr method concerns is described. First, the original analysis data such as the load, P, and contact stiffness, S, as a function of the indentation depth, h, are acquired by means of the continuous stiffness measurement (CSM) technique. By CSM, the complicating effects including indentation creep behaviour of metal materials as well as thermal drift on the measured results are avoided effectively. Then, the hardness of film-only is calculated via a material characteristic parameter, Pl, which is independent of the contact area, A, based on the constant modulus assumption method. In this way, the influences of the substrate contribution and material pile-up behaviour needn't be accounted for. Guided by above ideas, moreover, a 504 nm Au film on the glass substrate system was chosen to study. The results show that the hardness of An thin film is 1.6 +/- 1 GPa, which agree well with the literature. While the composite hardness measured by Oliver-Pharr method is between 2 similar to 3GPa, obviously, which is overestimated. This implies the present methodology is a more accurate and simple way for extracting the true hardness of the soft metallic thin films.