Phase evolution mechanism of SiC-Al-Si composite under flowing nitrogen at 1600 °C
Jishuo Han,Changhe Gao,Huaming Luo,Yong Li,Chenhong Ma,Xiaofang Wu
DOI: https://doi.org/10.1016/j.jallcom.2024.176419
IF: 6.2
2024-09-16
Journal of Alloys and Compounds
Abstract:Resin-bonded SiC-Al-Si composite was prepared and sintered under flowing nitrogen at 1600°C. By adjusting the Al/Si ratio, the controllable synthesis of various non-oxide reinforcing phases was achieved. The phase evolution mechanism was revealed, providing a theoretical foundation for the production and application of novel SiC-based refractory. As flowing nitrogen contained traces of oxygen, both Al and Si in the surface layer of the samples may be oxidized and nitrided. As the Al/Si mass ratio increased, the phase evolution in the surface layer of sintered samples followed this sequence: Si 5 AlON 7 →Si 3 Al 3 O 3 N 5 +AlN-SiC solid solution→AlN-SiC solid solution +Al 2 O 3 →Al 7 O 3 N 5 +Al 2 O 3 . As Al and Si consumed oxygen and generated non-oxides with multi-morphic sealed pores in the surface layer, the inner layer remained oxygen-free and low-nitrogen, leading to different phase evolution. As the Al/Si mass ratio increased, the phase evolution in the inner layer followed: Si 3 N 4 →AlN-SiC solid solution→AlN-SiC solid solution (content increase)→Al 4 SiC 4 . The synergistic toughening of various non-oxide resulted in a cold crushing strength of sintered samples exceeding 150 MPa. A reaction model was established.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering