Effects of Nitrogen Pressure on Microstructure and Mechanical Performance of Porous Silicon Nitride Ceramics

Zhang Jun-Xi,Xu Zhao-Yun,Wang Bo,Qin Yi,Yang Jian-Feng,Zhao Zhong-Jian,Hu Wei,Shi Zhi-Wei

DOI: https://doi.org/10.3724/sp.j.1077.2014.13531

2014-01-01

Abstract:Porous silicon nitride ceramic was fabricated by using alpha-Si3N4 as raw material and Y2O3 as a sintering additive, with nitrogen pressure of 0.12 MPa, 0.32 MPa and 0.52 MPa. Effects of the nitrogen pressure on grain morphology and mechanical properties of the resultant porous Si3N4 ceramics were characterized by SEM, XRD and flexural strength. With the increasing of nitrogen pressure, sintering shrinkage decreased, with a corresponding increased porosity. Due to the increase of nitrogen pressure, the viscosity of liquid phase increased due to increased N solubility, leading to the low densification in the sintering. Fibrous beta-Si3N4 grains were developed in the porous microstructure and the grain morphology and aspect ratio were greatly affected by the nitrogen pressures. The high viscosity of the liquid phase in nitrogen at high pressure led to restraining of the beta-Si3N4 nucleation, and preferential growth of beta-Si3N4. Due to the formation of elongated beta-Si3N4, flexural strength of the porous Si3N4 ceramic was improved by the increase of nitrogen pressure, while decreased with the increase of porosity. The porous Si3N4 ceramics with porosity of 58% and flexural strength of 140 MPa were obtained at the nitrogen pressure of 0.52 MPa.