Effects of α-Si3N4 seeds on properties of porous laminated silicon nitride ceramics

鲁元,杨建锋,陆伟忠,高积强,陕绍云

DOI: https://doi.org/10.3969/j.issn.2095-2783.2009.04.006

2009-01-01

Abstract:The porous silicon nitride ceramics were prepared in situ by the use of SiO2 through carbothermal reduction in nitrogen.There was a great lot of mass loss in this reaction,so it was expected to create the high porosity materials.The porosity controlled porous silicon nitride was obtained through changing the relative content of α-Si3N4,SiO2 and C.The three layered porous laminated silicon nitride ceramics composites were fabricated by this technique.The influences of composition of intermediate layer and interface between layers on the microstructure and mechanical properties of porous laminated silicon nitride ceramics composites were studied.When the difference in the linear shrinkage between the intermediate layer and superficial layer was large,even if the interface bonding strength between the layers was weak,the residual stress was favorable to mechanical properties.While the difference in the linear shrinkage between the intermediate layer and superficial layer became small,and the interface bonding strength between the layers changed from weak to strong,the flexural strength increased.So the porous laminated silicon nitride ceramics composites showed good mechanical properties.