Comparison of infiltrated ceramic fiber paper and mica base compressive seals for planar solid oxide fuel cells

Shiru Le,Kening Sun,Naiqing Zhang,Yanbin Shao,Maozhong An,Qiang Fu,Xiaodong Zhu

DOI: https://doi.org/10.1016/j.jpowsour.2007.03.014

IF: 9.2

2007-01-01

Journal of Power Sources

Abstract:Solid oxide fuel cells using non-glass sealants have become increasingly common. In this paper, fumed silica infiltrated ceramic fiber paper with pre-compression was compared with plain and pre-compressed at 10MPa hybrid mica as compressive seals. Leakage tests were measured under a 0.1–1.0MPa compressive load with the pressure gradient varying from 2 to 15kPa. The results demonstrated that the leakage rate of infiltrated fiber paper was 0.04sccmcm−1 for a 10kPa gradient, under 1.0MPa compressive load, while for mica it was 0.60 and 0.63sccmcm−1 which indicated that the infiltrated ceramic fiber paper showed a much lower leakage than mica. Long-term thermal cycling tests demonstrated that although the leakage of fumed silica infiltrated fiber paper was slightly higher than that of hybrid mica, it remained stable after 20 thermal cycles and no interlayer was needed. The mass loss of the fiber paper was 1.7×10−2mgcm−2h−1 in a hydrogen environment at 1073K for 200h. The leakage of infiltrated fiber paper remained about 0.06sccmcm−1 after reduction.