Sealing Properties of SOFC Stack Sealed by Mica and Glass Composite

于立安,童菁菁,韩敏芳

DOI: https://doi.org/10.14136/j.cnki.issn1673-2812.2012.02.002

2012-01-01

Abstract:Sealing has been identified as one of the key technologies for the development of planar solid oxide fuel cells（SOFCs）.In this work,mica and Bi2O3-BaO-SiO2-RxOy（R=K,Zn,Al2O3,etc.） glass were used as sealants for SOFC stack,by which cells supported by yttria-stabilized zirconia（YSZ） electrolyte were connected with interconnectors of SUS430 steel.Coefficient of thermal expansion（CTE）,seal performance and open circuit voltage（OCV） were determined by the experiments.Microstructure of the interface was studied by the scanning electron microscopy（SEM）.The average CTE of mica from room temperature to720℃ is 8.5×10-6 K-1 and the average CTE of the Bi2O3-BaO-SiO2-RxOy glass from 20℃ to 520℃ is 11.0×10-6 K-1.Thermal expansion of sealing materials was matched to the YSZ electrolyte and the steel interconnector.The layered structure of mica can relieve the stresses arising from different CTE values of the YSZ and SUS430 steel.Under high temperatures,mica also moderates the fluidity of the soft sealing glass materials.Good sealing properties have been found from gas-tightness experiments.The stack with the above sealing materials could keep OCV above 1.0V at operating temperature for 28 hours.Moreover,it was not obviously found the element diffusions in YSZ/sealant/SUS430 steel.This sealing method can therefore meet the application requirements of the SOFC stack.