Improvement of thermal cycle stability of YSZ-glass composite seals for intermediate temperature solid oxide fuel cell
Xiaochun Wang,Zhun Kou,Hao Wu,Yi Song,Xuepeng Zhao,Shanping Xu,Li Li
DOI: https://doi.org/10.1016/j.ceramint.2023.08.359
IF: 5.532
2023-10-06
Ceramics International
Abstract:Glass ceramic seals have been widely used in solid oxide fuel cell (SOFC). However, the sealing performance of seals is a big challenge for SOFC operating at high temperature. In this work, the gas tightness, chemical compatibility and thermal cycle stability of the glass-based seals with various proportions of YSZ and glass are evaluated and discussed. The study showed that when 20 wt% YSZ is added to H4 glass, the as-prepared glass ceramic seal (denoted as H4-20) exhibited extremely low leakage rate of 0.00171 sccm cm −1 under input pressure of 20.7 kPa and wide temperature range from 650°C to 800°C. In addition, the leakage rate of H4-20 glass ceramic seal below 0.004 sccm cm −1 was obtained after 10 thermal cycles at 750 °C. The SEM analysis indicated that the H4-20 glass ceramic seal could form well bonding interface between the interconnect/seal/cell. The above results prove the possibility of the H4-20 glass ceramic seals to be considered for intermediate temperature SOFC application.
materials science, ceramics