High-temperature synthesis of stable ordered mesoporous silica materials by using fluorocarbon-hydrocarbon surfactant mixtures.
Defeng Li,Yu Han,Jiangwei Song,Lan Zhao,Xianzhu Xu,Yan Di,Feng-Shou Xiao
DOI: https://doi.org/10.1002/chem.200400188
2004-01-01
Chemistry - A European Journal
Abstract:Highly ordered hexagonal mesoporous silica materials (JLU-20) with uniform pore sizes have been successfully synthesized at high temperature (150-220degreesC) by using fluorocarbon-hydrocarbon surfactant mixtures. The fluorocarbon-hydrocarbon surfactant mixtures combine the advantages of both stable fluorocarbon surfactants and ordered hydrocarbon surfactants, giving ordered and stable mixed micelles at high temperature (150-220degreesC). Mesoporous JLU-20 shows extraordinary stability towards hydrothermal treatment (100% steam at 800degreesC for 2 h or boiling water for 80 h), thermal treatment (calcination at 1000degreesC for 4 h), and toward mechanical treatment (compressed at 740 MPa). Transmission electron microscopy images of JLU-20 show well-ordered hexagonal arrays of mesopores with one-dimensional (M) channels and further confirm that JLU-20 has a two-dimensional (2D) hexagonal (P6mm) mesostructure. Si-29 HR MAS NMR spectra of as-synthesized JLU-20 shows that JLU-20 is primarily made up of fully condensed Q(4) silica units (delta = - 112 ppm) with a small contribution from incompletely cross-linked Q(3) (delta = - 102 ppm) as deduced from the very high Q(4)/Q(3) ratio of 6.5, indicating that the mesoporous walls of JLU-20 are fully condensed. Such unique structural features should be directly attributed to the high-temperature synthesis, which is responsible for the observed high thermal, hydrothermal, and mechanical stability of the mesoporous silica materials with well-ordered hexagonal symmetry. Furthermore, the concept of "high-temperature-synthesis" is successfully extended to the preparation of three-dimensional (3D) cubic mesoporous silica materials by the assistance of a fluorocarbon surfactant as a co-template. The obtained material, designated JLU-21, has a well-ordered cubic Im3m mesostructure with fully condensed pore walls and shows unusually high hydrothermal stability, as compared with conventional cubic mesoporous silica materials such as SBA-16.