Abstract:Hierarchical meso-macroporous materials have attracted much attention due to their potential applications in catalysis, sorption, and separation. The incorporation of interconnected macropores in mesoporous materials is very useful because macropores can favor mass transfer and reduce transport limitations. However, it still remains a challenge to fabricate ordered mesoporous channels in the bicontinuous macroporous framework walls. This paper reports a double-templating route based on a sol-gel method to prepare hierarchical meso-macroporous silica monoliths. The obtained material shows a bicontinuous macroporous structure with highly ordered meso-channels distributing inside the macroporous skeleton walls. The bimodal pore structure was formed Under the action of the two templates. The organic polymer was added to induce a phase separation taking place at the sol-gel transition and thus form the bicontinuous macroporous structure. Meanwhile, a nonionic surfactant was introduced to template the formation of ordered mesostructure inside the macroporous skeleton walls. As characterization by scanning electron microscopy, transmittance electron microscopy, N-2,, physisorption, and X-ray diffraction, the resulting silica monolith exhibits Specific Surface area as high as 880 m(2)/g and pore volume as large as 1.2 cm(3)/g. The hexagonally ordered mesopores are highly centered at 5.8 nm. Besides, through optimizing the synthesis procedure, the monolith morphology of the resulting materials can be perfectly preserved during the wet gel drying process, and thus a crack-free hierarchical silica monolith with centimeter scale can be obtained.

Double-Mesopore V-Msu-X Silica and Its Pure Siliceous Derivative Prepared by One Synthesis System

Preparation of Mesoporous Molecular Sieves Al-Msu-S Using Ionic Liquids As Template

Synthesis and Coating of Ordered Mesoporous Silica

Synthesis of ultrastable ordered mesoporous aluminosilicates molecular sieves with “hard template”

Synthesis of Si-based mesoporous materials with different structural regularity

Sol-gel synthesis of methyl-modified mesoporous materials with dual porosity

Thioether‐bridged Mesoporous Organosilicas: Mesophase Transformations Induced by the Bridged Organosilane Precursor

A Mesoporous ZSM-5 Zeolite Synthetized by a Novel Double Long-Alkyl-Chain Organosilane Template

Mesoporous silica obtained with methyltriethoxysilane as co-precursor in alkaline medium

Silicone Surfactant Templated Mesoporous Silica

Triblock Copolymer and Poly(Ethylene Glycol) As Templates for Monolithic Silica Material with Bimodal Pore Structure

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

Preparation of Ordered 2-D Hexagonal Mesoporous Silica with Ultra Thick Pore Walls Using a Novel Nonionic Organosilicon Surfactant

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Large-Pore Mesoporous Silica with Three-Dimensional Wormhole Framework Structures

Acid Catalyzed Synthesis of Ordered Bifunctionalized Mesoporous Organosilicas with Large Pore

A Systematic Investigation Of The Formation Of Ordered Mesoporous Silicas Using Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate) As The Template

Synthesis of Silicate Materials with Micro/Macroporous Bimodal Pore Systems

Core-template-free Synthesis of Molecularly Ethane-Bridged Hollow Mesoporous Silica Spheres from Acid-Hydrolyzed Precursor

Synthesis of Dual‐Mesoporous Silica Using Non‐Ionic Diblock Copolymer and Cationic Surfactant As Co‐Templates