Abstract:The 2195 Al-Li alloy, as one of the representative third-generation Al-Li alloys, has extensive applications in lightweight aerospace structures. In this paper, the anisotropy in mechanical properties and microstructure evolution of 2195 Al-Li alloy sheets were investigated under a strain rate of 0.01, 0.1, 1 s-1 and a temperature of 440 and 500 °C. Experimental results showed that the hot tensile properties of the 2195 Al-Li alloy sheet exhibited a strong dependence on loading directions. The peak stress (PS) and elongation (EL) along the rolling direction (RD) were larger than the transverse direction (TD). For the tests carried out at 440 °C-1 s-1, the PS values of the sheets stretched along the RD and TD are 142.9 MPa and 110.2 MPa, respectively. And, most of the PS anisotropy values are larger than 15%. The anisotropy in EL is less significant than in PS. All the differences are about 10%. Moreover, dimples in the samples stretched along RD were more and deeper than those along TD at 440 °C. The fracture morphology along RD and TD were similar, and both were cleavage fractures at 500 °C. Particularly, the fractions of high angle grain boundaries (HAGBs) along TD were all about 5% larger than those of RD. And, there were more small-sized continuous dynamic recrystallization (CDRX) grains inside the initial grains and discontinuous dynamic recrystallization (DDRX) grains featured with the local bulge of grain boundaries along TD. This was due to the smaller average Schmid factor and the vertical EL trend of the initial grains when the samples were stretched along TD. A model of grain evolution during the dynamic recrystallization (DRX) along RD and TD was proposed based on EBSD results. The Schmid factor and banded structure had a more prominent effect on the hot ductility of the 2195 Al-Li alloy compared with the degree of DRX, thus presenting a higher EL and better hot ductility along RD.

Serrated Flow Behavior in 2090 Al–Li Alloy Influenced by Texture and Microstructure

Serrated Flow Behavior in Commercial 5019 Aluminum Alloy

The effect of temperature on the serrated flow in AA5456 alloys

Thermal stability and its effects on the mechanical properties of rapidly solidified Al-Ti alloys

Dislocation Density-Based Model for Flow Behavior of a Near-α Titanium Alloy Considering Effects of Initial Lamellar Thickness

On temperature and strain-rate dependence of flow serration in HfNbTaTiZr high-entropy alloy

Quasi-static and dynamic response, and texture evolution of two overaged Al 7056 alloy plates in T761 and T721 tempers: Experiments and modeling

Effect of Solute Concentration on the Serrated Flow in Solution-Treated Al–4%Cu Alloys

Characterization and constitutive analysis-based crystal plasticity of warm flow and fracture behaviours of 2060 Al-Cu-Li alloy

Influence of Precipitates on the Serrated Yielding in Al-Cu-Mg Alloy and Microscopic Experiment Investigation

Effect of Initial Orientation on the Anisotropy in Microstructure and Mechanical Properties of 2195 Al-Li Alloy Sheet during Hot Tensile Deformation

Influence of Nature Aging on Serrated Yielding of 6061 Al-based Alloy

Anisotropic Mechanical Behavior and Microstructural Characteristics of AA2099-T83 Alloy Sheet: Experiment and Simulation

Statistical analysis of serrated flows in CoNiV medium-entropy alloy

Microstructural evolution and mechanical properties of the rapidly-solidified and hot-extruded 2196 Al-Li alloy

Influence of Solute Cloud and Precipitates on Spatiotemporal Characteristics of Portevin-Le Chatelier Effect in A2024 Aluminum Alloys

Investigation of Tensile Flow Behavior of Al–Mg Alloy at Warm Temperature: Constitutive Modelling and Microstructural Evolution

Mechanical properties of Al–Li alloys Part 1 Fracture toughness and microstructure

Experimental Study and Mechanism Analysis of the Serrated Plastic Instability of Alloy Materials

Anisotropy in creep-aging behavior of Al–Li alloy under different stress levels: experimental and constitutive modeling

Microstructure evolution and mechanical properties of Al-Cu-Li alloys with different rolling schedules and subsequent artificial ageing heat treatment