Formation and Its Mechanism of TiO2 Nanorod Array on Surface of Titanium Substrate
Huang Shanshan,Ning Chengyun,lt,strong gt,Tan Guoxin lt,Zhen Huade,Li Dan,Guo Yuanjun,Xiong Wenming,Ge Yongmei
2012-01-01
Rare Metal Materials and Engineering
Abstract:High density and uniform TiO2 nanorod array film on Ti plate was prepared via an anodization of constant current method in NH4F aqueous solution. The microstructure, elemental composition, combined valence state and the phase of samples were investigated by field-emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectrometry and X-ray diffraction (XRD). It is found that the TiO2 nanorod array was formed which was of uniform distribution, orderly arrangement and oriented growing along the vertical direction at the surface layer of Ti matrix. The mean diameters of nanorods were 25.68 nm, the length 91.35 nm, the aspect ratio 3.56 and the average density 189 similar to 197 per mu m(2). The phase of TiO2 nanorod array was transformed to anatase with the crystallinity 28.6% after heat-treating at 550 degrees C, which was oriented growing along the (110).