Abstract:Self-organized TiO2 nanotube arrays with micro-scale length were prepared on fluorine-doped tin oxide (FTO) conducting glass in NH4F/glycerol electrolyte by electrochemical anodization of pure titanium films deposited by radio frequency magnetron sputtering (RFMS) at room temperature. The samples were characterized by means of field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and photoelectrochemistry methods. The results showed that Ti films prepared at the condition of Ar pressure 0.5 Pa, power 150 W, and 0.5 h at room temperature possessed the zone T model structure with good homogeneity and high denseness. When the anodization time was prolonged from 1 to 3 h at the voltage of 30 V, the pore diameter of TiO2 nanotubes increased from 50 to 75 nm, and the length increased from 750 to 1100 nm and then gradually decreased to 800 nm, while their wall morphology changed from smooth to rough. Also with increasing the anodization voltage, the pore diameter became larger, and the remaining oxide layer reduced, which could be easily removed by ultrasonic-chemical cleaning in 0.05% (w, mass fraction) diluted HF solution. Moreover, the photocurrent response curves and electrochemical impedance spectroscopy (EIS) results indicated that UV-illumination clearly enhanced the effective separation of the electron-hole pairs and the crystallized electrodes from the annealing treatment of as-anodized electrodes at 450 °C exhibited a better photoelectrochemical performance.

Preparation and Characterization of TiO<SUB>2</SUB> Nanotube Arrays by Anodic Oxidation Method: Preparation and Characterization of TiO<SUB>2</SUB> Nanotube Arrays by Anodic Oxidation Method

Fabrication of TiO2 Nanotube Arrays by a Two-Step Anodic Oxidation

Preparation and Characterization of TiO2 Nanotube Arrays Via Anodization of Titanium Films Deposited on FTO Conducting Glass at Room Temperature

Preparation of TiO2 Nanotube Arrays by Anodic Oxidation

Fabrication and Properties of Tio2 Nanotube Arrays Using Glycerol-Dmso-H2o Electrolyte

Fabrication of highly ordered TiO2 nanotube arrays via anodization of Ti-6Al-4V alloy sheet.

Electrochemical Fabrication and Formation Mechanism of Tio2 Nanotube Arrays on Metallic Titanium Surface

Preparation and Characterization of TiO2 Nanotube Arrays on Porous Titanium

Controllable Preparation of TiO2 Nanotube Arrays on Ti Foil Substrates

Preparation Of Tio2 Nanotube Arrays And Their Photoeleetrochemical Properties

Electrochemical Fabrication and Formation Mechanism of TiO~ 2 Nanotube Arrays on Metallic Titanium Surface

Morphology of TiO_2 Nanotube Arrays Prepared by Anodic Oxidation

Fabrication of TiO2 Nanotube Arrays via Electrochemical Anodization in NH4F/H3PO4 Electrolyte Solution System

Preparation of TiO_2 Nanotube Arrays and Their Photoelectrochemical Properties

Characterization of TiO 2 Nanotube Arrays Prepared Via Anodization of Titanium Films Deposited by DC Magnetron Sputtering

Fabrication of TiO2 Nanotube Arrays by Electrochemical Anodization in an NH4F/H3PO4 Electrolyte

Fabrication of TiO<sub>2</sub> Nanotube Arrays in Ethylene Glycol Electrolyte by the Electrochemical Anodization Method

Anodic Oxidation Mechanism and Annealing Influence of TiO2 Nanotubes Arrays

Fabrication and Microstructure of TiO2 Nanotube Arrays Membranes

TiO2 nanotube arrays prepared by anodic oxidation method

Preparation of Well-Aligned TiO2 Nanotubes with High Length-Diameter Aspect Ratio by Anodic Oxidation Method