Abstract:Uniform and highly ordered TiO2 nanotube arrays were fabricated by the electrochemical anodic oxidation on Ti-6Al-4V surface, using graphite plate as cathode and ethylene glycol (EG) with addition of a certain amount of H2O and NH4F as electrolyte, and the anodization voltage went up to a presetting voltage by stepwise increment. The morphology, structure and composition of TiO2 nanotube arrays were characterized by SEM, EDS, XRD and XPS. The formation process of TiO2 nanotubes was introduced in brief. The experiments were arranged by an orthogonal experiment method and the experimental results showed that the formation of TiO2 nanotube arrays was influenced by not only each factor (F- content, H2O content, external voltage and duration), but also cross correlation among the four factors. The optimal condition was F- content 0.2 wt%, H2O content 4 vol%, external voltage 40 V and duration 1 h in the studied electrochemical system, and the length of obtained nanotubes was 1.5 microm, the outer diameter was approximately 100 nm and the aspect ratio was 15. As-formed nanotube arrays were amorphous and changed to anatase TiO2 after annealed at 500 degrees C for 2 h in air ambience. XPS survey spectra revealed the surface of as-formed nanotube arrays containing Ti, O, C, F and N. The nanotube arrays on Ti-6Al-4V surface with better thermo-stability and crystallinity would have great potential in biomaterials.

Preparation of Well-Aligned TiO2 Nanotubes with High Length-Diameter Aspect Ratio by Anodic Oxidation Method

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

TiO2 nanotube arrays prepared by anodic oxidation method

Morphology of TiO_2 Nanotube Arrays Prepared by Anodic Oxidation

Preparation of TiO2 Nanotube Arrays by Anodic Oxidation

Fabrication of TiO2 Nanotube Arrays by a Two-Step Anodic Oxidation

Preparation and Characterization of TiO<SUB>2</SUB> Nanotube Arrays by Anodic Oxidation Method: Preparation and Characterization of TiO<SUB>2</SUB> Nanotube Arrays by Anodic Oxidation Method

Effect of Two-Step Anodization on Structure of TiO2 Nanotube Arrays

High Ratio-Aspect Titania Nanotube Array Prepared by Anodic Oxidation Method

Titanium oxide nanotube arrays prepared by anodic oxidation

Study on preparation of TiO_2 nanotube arrays by anodizing processes

Fabrication of highly ordered TiO2 nanotube arrays via anodization of Ti-6Al-4V alloy sheet.

Preparation and Doping of Anodic Tio2 Nanotube Array

Preparation of High-ordered TiO2 Nanotube Arrays

PREPARATION AND CHARACTERIZATION OF TITANIA NANO TUBE ARRAY BY ANODIC OXIDATION

In-situ preparation of multi-layer TiO2 nanotube array thin films by anodic oxidation method

Preparation of TiO2 Nanotubes Array on Ti Meshes by Anodic Oxidation

The Influence of Oxidation Time on the Morphology of Titania Nanotube Arrays

Controllable Preparation of TiO2 Nanotube Arrays on Ti Foil Substrates

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

Preparation of TiO_2 Nanotube Arrays by Anodization for Industrial Application