Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Fabrication and Properties of Tio2 Nanotube Arrays Using Glycerol-Dmso-H2o Electrolyte

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Synthesis of TiO<sub>2</sub> Nanotube Arrays Through Multistep Anodization

Fabrication of Titanium Oxide Nanotube Arrays by Anodic Oxidation

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Fabrication of Highly-Oriented TiO2 Nanotube Arrays and Its Application in Dye-Sensitized Solar Cells

Crystal phase transition and properties of titanium oxide nanotube arrays prepared by anodization

Morphology of TiO_2 Nanotube Arrays Prepared by Anodic Oxidation

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO2 Nanotube Arrays

TiO<sub>2</sub> Nanowires/Nanobelts Originating from Anodically Grown Nanotube Arrays

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO<sub>2</sub> Nanotube Arrays

Fabrication and Field Emission Characteristics of TiO2 Nano-Tube Arrays

Fabrication of multi-sectional TiO 2 nanotube arrays by anodization

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Anodization Fabrication of Highly Ordered Tio2 Nanotubes

Facile Fabrication, Characterization, and Enhanced Photoelectrocatalytic Degradation Performance of Highly Oriented Tio2 Nanotube Arrays

Fabrication of open-ended TiO2 nanotube arrays by anodizing a thermally evaporated Ti/Au bilayer film

Highly Ordered TiO2 Nanotube Arrays with Engineered Electrochemical Energy Storage Performances

Synthesis And Photovoltaic Application Of High Aspect-Ratio Tio2 Nanotube Arrays By Anodization