Formation and Its Mechanism of TiO_2 Nanorod Array on Surface of Titanium Substrate

Huang Shanshan,Ning Chengyun,Tan Guoxin,Li Dan,Guo Yuanjun,Xiong Wenming,Ge Yongmei

2012-01-01

Rare Metal Materials and Engineering

Abstract:High density and uniform TiO2 nanorod array film on Ti plate was prepared via an anodization of constant current method in NH4F aqueous solution.The microstructure,elemental composition,combined valence state and the phase of samples were investigated by field-emission scanning electron microscopy(FE-SEM),X-ray photoelectron spectrometry and X-ray diffraction(XRD).It is found that the TiO2 nanorod array was formed which was of uniform distribution,orderly arrangement and oriented growing along the vertical direction at the surface layer of Ti matrix.The mean diameters of nanorods were 25.68 nm,the length 91.35 nm,the aspect ratio 3.56 and the average density 189～197 per μm2.The phase of TiO2 nanorod array was transformed to anatase with the crystallinity 28.6% after heat-treating at 550 ℃,which was oriented growing along the(110).