Effects of Structural Features of Titania Nanotube on Its Photoelectrocatalytic Performance

LI Yun-lin,ZHANG Chao,YANG Jie,ZHOU Ming-hua
DOI: https://doi.org/10.3969/j.issn.1001-9731.2013.z1.028
2013-01-01
Abstract:The effect of structural features of titania nanotube arrays fabricated by anodization under different anodizing voltages and anodizing times on its photoelectrocatalytic performance was investigated.Characterized by transmission electron microscopy,X-ray diffraction,X-ray photoelectron spectroscopy,the photoelectrochemical properties,the photoelectrocatalytic activity of titania nanotube arrays with different nanostructure features,the reaction kinetics performance of its for the degradation of methyl orange were investigated.These results demonstrated that the aspect ratio of titania nanotube arrays has a maximum impact on its photoelectrocatalytic performance.The nanotube length and diameter of titania nanotubes increased with the increase of anodizing voltage and anodizing time,and the wall thickness of titania nanotube decreased with the increase of anodizing voltage.Titania nanotube with tube length of 25.85μm,wall thickness of 10.23nm,roughness factor of 175 and aspect ratio of 178 fabricated at 60V for 6h possessed the maximum photocurrent density of 4.8×10-2mA/cm2,and the maximum first order reaction kinetic constant of degradation of methyl orange was 2.26×10-3min-1.
What problem does this paper attempt to address?