Temperature Coefficient-Adjustable Dielectric Ceramics Near the Nominal Composition Ba2Ti3Nb4O18

Dong Guo,Zhiyuan Ling,Xing Hu
DOI: https://doi.org/10.1016/j.ceramint.2007.07.004
IF: 5.532
2008-01-01
Ceramics International
Abstract:Dense dielectric ceramics with the nominal composition Ba2Ti3Nb4O18 were obtained by solid-state reaction. Although the XRD results showed the single phase in Ba2Ti3Nb4O18, the micro-structural analysis confirmed the existence of the secondary phase Ba3Ti4Nb4O21. Excellent temperature-stable dielectric ceramics were obtained with the nominal composition Ba2Ti3Nb4O18, where ɛr=38, tanδ∼0.0003, and τɛ∼2ppm/°C (all measured at 1MHz). The τɛ value can be adjusted from −6 to 17ppm/°C near the vicinity of nominal composition Ba2Ti3Nb4O18 by changing the Ti content. The microwave dielectric properties of the nominal composition Ba2Ti3Nb4O18 were as follows: ɛr=38.1, Qf=14,227GHz, and τf=−11ppm/°C.