Abstract:The Ti-based bulk metallic glasses (BMG) with high Ti content (>50 at.%) have attracted wide attention for their outstanding mechanical properties, despite their glass forming ability (GFA) is still relatively poor. Here the (Ti55Zr15Be20Ni10)(100-x)Cu-x(x = 2, 4, 6, 8 and 10 at.%) BMGs were designed and prepared by copper mold casting. The critical diameter of the original alloy could be enhanced from 5 mm to 10 mm with the Cu addition of 4 at.%, which is the first reported centimeter-sized Ti-based BMG with Ti content more than 52 at.%. In addition, all the as-prepared BMGs exhibited higher yield strength (above 2000 MPa). And the supercooled liquid range of the as-prepared Ti-based BMGs were enlarged from 35 K to 74 K by Cu addition. Electrochemical measurements showed that the BMGs with Cu addition of 0-6 at.% exhibited much higher pitting potentials (over 573 mV/SCE) than that of 304 stainless steel (304SS) in 3.5 wt% NaCl aqueous solution. And The XPS analysis revealed that the Cu addition might lead to the enrichment of Cu and the deficiency of Ti, Zr, Ni elements in passive film, which could induce the worse corrosion resistance of the Ti-based BMGs with high Cu content. The results indicate that the developed Ti-based BMGs possess good GFA, mechanical properties and corrosion resistance. (C) 2017 Elsevier B.V. All rights reserved.

Effects of Ni Addition on Glass Forming Ability and Mechanical Properties of Mg_(65)Cu_(25)Tb_(10) Bulk Amorphous Alloy

Glass-forming ability and thermal stability of Gd55-xNd xCo20Al25 metallic glass

The Effect of Ni Substitution on the Glass-Forming Ability and Mechanical Properties of Mg–Cu–Gd Metallic Glass Alloys

PREPARATION AND PROPERTIES OF BULK AMORPHOUS Fe-Ni-P-B-Ga ALLOYS

Effect of Ti addition on supercooled liquid region and glass forming ability of bulk amorphous Zr60Cu20Ni10-xAl10Tix alloys

Effect of Chemical Composition on the Thermoplastic Formability and Nanoindentation of Ti-Based Bulk Metallic Glasses

Effects Of Ta, Nb And Mo Additions On Glass-Forming Ability Of Ti50ni20cu25sn5 Amorphous Alloy

Formation and Compressive Properties of A Ni-Ti-Zr-Al-Cu-Si Amorphous Alloy

Effects of Ga,In additions of the Glass Forming Ability of Fe40Ni40P14B6 Eutectic Alloy

Glass-forming Ability and Thermal Stability of Fe-Co-Ni-Zr-Mo-W-B Bulk Amorphous Alloys

STRUCTURAL RELAXATION AND MECHANICAL PROPERTIES OF Mg-Cu-Ni-Gd AMORPHOUS ALLOYS

Effects of the partial substitutional alloying elements on the crystallization behavior of Mg65Cu25Gd10 metallic glass: Ag versus Ni

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Effect of Ag substitution for Ti on glass-forming ability, thermal stability and mechanical properties of Zr-based bulk metallic glasses

Effect of Co Addition on the Glass-Forming Ability and Mechanical Properties of Ti-Zr-Be-Cu-Co Bulk Amorphous Alloys

Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses

Effect of Nb Addition on the Glass-Forming Ability, Soft-Magnetic Properties and Mechanical Properties of CoFeNiBSiNb Bulk Glassy Alloys

Effect of Ni substitution for Ga on the polycrystalline Ni-Mn-Ga-Gd high-temperature shape memory alloys

Effect of Nb-Content on Mechanical Properties of (Ni<sub>47</sub>Ti<sub>44</sub>)<sub>100-x</sub>Nb<sub>x</sub> Shape Memory Alloys

Effect of the Ti content on microstructure and properties of Ni53Mn23.5Ga23.5-xTix ferromagnetic shape memory alloy

Effects of Cu Addition on the Glass Forming Ability and Corrosion Resistance of Ti-Zr-Be-Ni Alloys