Abstract:The thermal shock damage behavior of SiC/SiC‐EBC is systematically investigated. Coating cracking or even peeling occurs due to thermal stress mismatch, which acts as channels for oxygen, leading to oxidative damage of Si coatings and partial SiC/SiC substrate. However, delamination within SiC/SiC substrate is the main cause of SiC/SiC‐EBC failure. Thermal shock damage is a key issue for the stable service of SiC/SiC with environmental barrier coating (EBC) in aero‐engines. The thermal shock damage behavior of SiC/SiC with barium‐strontium aluminosilicate (BSAS)‐based EBC in an air atmosphere quenched by air and water media between RT and 1200 °C is systematically investigated. After 600 thermal shock cycles, cracks form in the EBC due to a sharp increase in the internal thermal stresses, and a SiO2 TGO layer is formed on the Si bonding coat. Based on the TGO thickness, damage within BSAS/mullite coatings is quantified by the oxygen permeability (2.541 × 10−11 mol·(atm cm s)−1), which is increased by 2.5 times compared to static oxidation. Despite cracking damage occurring in the SiC matrix of SiC/SiC substrates, the load‐bearing capability of SiC fibers is improved due to the modulus matching of the fiber/matrix. Oxidation damage is dominated the degradation of the performance of SiC/SiC substrates, whose flexural strength is decreased by 15% after 600 cycles. In the thermal shock test quenched by water media, the strength retention of SiC/SiC‐EBC is below 60%, and an increase in internal defects and even delamination of the SiC/SiC substrate are the main reasons for the thermal shock failure of SiC/SiC‐EBC.

The Behavior of Coatings and SiCf/SiC Composites under Thermal Shock

Thermal Shock Behavior of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Influence of Thermal Shock on the Mechanical Behavior of Si-SiC Coated Carbon/Carbon Composites

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

Finite Element Simulation of Stress Distribution and Development of C-F/Sic Ceramic-Matrix Composite Coated with Single Layer Sic Coating During Thermal Shock

The High Temperature Thermal Shock Performance of Si-Ti-Cr Silicide System Coating on Nb-Hf Alloy Surface in Atmosphere and Vacuum

Thermal shock behavior and oxidation resistance of novel SiC nanowires+Si/Yb2Si2O7-Si/Yb2Si2O7 environmental barrier coatings

Mechanical and Thermal Shock Properties of Cf/SiBCN Composite: Effect of Sintering Densification and Fiber Coating

Ablation Behavior and Mechanism of Sicf/C-F/Sibcn Ceramic Composites with Improved Thermal Shock Resistance under Oxyacetylene Combustion Flow

Mechanical /thermal Shock Properties and Failure Mechanisms of Cf/SiBCN Composites Effect of Sintering Densification and Fiber Coating

Thermal Shock and Ablation Behavior of Α-Cordierite Glass-Ceramic Coating on Porous BN/Si2N2O Ceramic

Mechanical and thermal shock properties of C f /SiBCN composite: Effect of sintering densification and fiber coating

Thermal Shock and Residual Strength Testing of SiC/SiC Composite Braided Tubes

Fabrication of porous SiC nanostructured coatings on C/C composite by laser chemical vapor deposition for improving the thermal shock resistance

Thermal Shock Damage and Failure Mechanism of 2D Laminated SiC/SiC with Barium‐Strontium Aluminosilicate‐Based Environmental Barrier Coating

Cyclic Thermal Shock Damage Behavior in CVI SiC/SiC High-Pressure Turbine Twin Guide Vanes

Experimental Study on the Dynamic Mechanical Behaviors of Silicon Carbide Ceramic after Thermal Shock

In-Situ formation of the BSG bubbles toward SiC/SiC composites protection mechanisms under thermal shock treatment

Thermal shock behavior of nanostructured and microstructured thermal barrier coatings on a Fe-based alloy