Abstract:High-reflectance ohmic contacts to p-GaN are the key for Flip-chip ultra-violet light emitting diode (UV-LED) to improve the external quantum efficiency (EQE), so the kinds of metal or alloy film both ohmic contact and the reflector of light are important to choose the appropriate high-reflectance and low-resistance ohmic contact to p-type GaN. The GaN-based LED samples used were grown by Metalorganic Chemical Vapor Deposition (MOCVD). Four different metal films were deposited on the surfaces of p-GaN and annealed Ni/Au alloy. The thickness of these metal films varied from 30 nm to 840 nm. The reflectance and transmittance of the samples were mea- sured by WGS-9 system. The 2θ scans XRD and surface AFM images of the samples were also observed. As results, when the films' thickness under the 130 nm the reflectance of Ag-deposited samples increased with the increasing thickness and the transmittance decreased at wavelength of 400 nm. The reason of the increasing of reflectance is the reduction of the light transmitted through the films. When the films' thickness over 130 nm, the reflectance of Ag-deposited samples decreasing. From the results of XRD and AFM, the metal film formed multi-layers film and the roughness R_a and R_q increased with the increasing thickness. It is suggested that the diffusion of the multi-layers films is the main reason of reduction of reflectance with the films thickness increasing. Other metal films show the same characteristics as the Ag-deposited films. From the result of reflectance, Al and Ag are the suitable candidates for the reflector, but it is reported that the single Al or Ag films don't make good ohmic contacts on p-GaN. So a thin annealed Ni/Au is adopted to interspersed between the Al or Ag reflector and the p-GaN in order to provide efficient hole injection into the device. From the results of reflectance and I-V curves of Ni/Au/Ag and Ni/Au/Al, the I-V characteristics of Ni/Au/Ag and Ni/Au/Al contacts are similar to this of Ni/Au annealed. However the reflectance of Ni/Au/Ag and Ni/Au/Al contacts is three times higher than that of Ni/Au at wavelength of 400 nm. These results demonstrated that Ni/Au/Ag and Ni/Au/Al can be used as high-reflectance and low-resistance p-GaN ohmic contacts for flip-chip UV-LEDs

The Role of Ni and Au on Transparent Film of Blue LEDs

GaInN Light-Emitting Diodes with Omni-Directional Reflector Using Nanoporous SnO2 Film

Ohmic Contact Characteristics of AlGaN-based Deep-ultraviolet Light-emitting-diodes with NiAu Transparent Electrode

Optical and Electrical Properties of the LED Using ZnO:Ga Film As Current Diffusion Layer by Sol-gel Technique

High-reflectance Ohmic Contacts to P-Gan of GaN-based Violet LEDs

Transparent (Ni,Au)/ZnO:Al-Based Ohmic Contacts to p-Type GaN as an Insight into the Role of Ni and Au in Standard p-Type GaN Contacts

Evaluation of Ti/Al/Ni/Au ohmic contact to n-AlGaN with different Ti/Al thickness for deep ultraviolet light emitting diode

Ohmic Contact of High Reflectivity on P-Type GaN

Highly Reflective Ni/Ag/Pt/Au Ohmic Contacts To P-Gan With Ito Interlayer

Thermal Annealing Effects on Ni/Au Contacts to P Type Gan in Different Ambient

Performance Comparison of Pt/Au and Ni/Au Schottky Contacts on Alxga1-X N/Gan Heterostructures at High Temperatures

Microstructure Evolution of Oxidized Ni/Au Ohmic Contacts to P-Gan Studied by X-Ray Diffraction

Improving the Performance of Free-pGaN Deep-Ultraviolet Light-Emitting Diodes by Embedding Self-Assembled Ni Nanoparticles Between p-AlGaN/p-Electrode

Performances of GaN-based LEDs with AZO Films As Transparent Electrodes

Light Extraction Efficiency Enhancement of GaN-based Blue LEDs Based on ITO/ InxO Ohmic Contacts with Microstructure Formed by Annealing in Oxygen.

Study of Ti/Au, Ti/Al/Au, a nd Ti/Al/Ni/Au ohmic co ntacts to n-GaN

Effects of Oxidation by O2 Plasma on Formation of Ni∕Au Ohmic Contact to P-Gan

Study of Ti/Au, Ti/Al/Au, and Ti/Al/Ni/Au ohmic contacts to n -GaN

Investigation on the formation mechanism and diffusion of the electrode metal of oxidized Au/Ni/p-GaN ohmic contact in different alloying time

The Influences of Sputtered AlN Buffer Layer on AlInGaN Based Blue and Near‐ultraviolet Light Emitting Diodes

Analysis of the Mechanisms by Which Sputtered AlN Nucleation Layers Enhance the Performance of Red InGaN-based LEDs