Microstructures and thermoelectric properties of Co-doped iron disilicides prepared by rapid solidification and hot pressing

H.Y. Chen,X.B. Zhao,C. Stiewe,D. Platzek,E. Mueller

DOI: https://doi.org/10.1016/j.jallcom.2006.06.080

IF: 6.2

2007-01-01

Journal of Alloys and Compounds

Abstract:Iron disilicide based alloys Fe0.94Co0.06Si2.00 were prepared by rapid solidification and hot uniaxial pressing. The effects of pre-annealing of the powders and hot pressing temperature on the microstructures and thermoelectric properties were investigated. X-ray diffraction and scanning electron microscopy show that after pre-annealing at 800°C for only 2h, the high temperature phases (α-Fe2Si5 and ɛ-FeSi) in the rapidly solidified powders have been completely transformed to β-FeSi2 phase, while the fine grain structures were maintained. It is found that the grain growth during hot pressing was successfully suppressed for the pre-annealed samples, especially at a lower pressing temperature of 880°C. The Seebeck coefficient was markedly enhanced by the pre-annealing treatment, also by a lower pressing temperature, while both the electrical conductivity and the thermal conductivity were decreased by them. The maximum dimensionless figure of merit ZT=0.25 at 908K was obtained for Fe0.94Co0.06Si2.00, which is pre-annealed, followed by hot pressing at 880°C with 70MPa for 30min.