Preparation of BiFeO_3 Powders by Co-precipitation Method

谈国强,博海洋,苗鸿雁,夏傲,贺中亮

DOI: https://doi.org/10.16553/j.cnki.issn1000-985x.2010.01.039

2010-01-01

Abstract:BiFeO3 powders were prepared by co-precipitation method.The precursor was prepared by co-precipitation using Fe(NO3)3·9H2O and Bi(NO3)3·5H2O as starting materials,ice vineqar acid as solvent and citric acid as chelating agent.Then the BiFeO3 powder was obtained after annealed at a certain temperature.The powders were characterized by X-ray diffraction (XRD),field emission scanning electron microscope (FE-SEM).The effect of citric acid content and annealing temperature on the structure and morphology was disscussed.The results showed that grains began to grow at 450 ℃,which was made up of BiFeO3 and some other crystal phases;the pure BiFeO3 powder was acquired when the annealing temperature was 600 ℃;the particle size of the samples decreases from 14.21 nm to 11.65 nm with the adding amount of ice vineqar acid increased from 1 mL to 1.8 mL.EDS spectrum analysis proved that the powder was composed of three elements-Bi,Fe and O.