Abstract:In this study, porous silicon carbide ceramics were prepared by using silicon carbide as the main material and sodium carboxymethyl cellulose (CMC) as the pore-forming agent. SiO2-Y2O3-Al2O3 and SiO2-kaolin were used as the builders respectively. This study is about the effect of SiO2-Y2O3-Al2O3 and SiO2-kaolin content on the structure and mechanical properties of porous silicon carbide. SiO2-Y2O3-Al2O3 and SiO2-kaolin affect the porosity, hardness and flexural strength of silicon carbide porous ceramics. In this experiment, the porosity of porous ceramics was measured by Archimedes method. The hardness was measured by Rockwell hardness tester. The flexural strength was measured by universal testing machine. The results show that the properties of silicon carbide porous ceramics prepared by SiO2-Y2O3-Al2O3 are better than that of SiO2-kaolinite when the SiO2 -Y2O3-Al2O3 content is 20%. With SiO2-Y2O3-Al2O3 as the combustion agent, porous ceramic with better performance can be prepared at 1500 °C. When the SiO2-Y2O3-Al2O3 content is 20%, the prepared silicon carbide porous ceramics has a large porosity and excellent mechanical properties, the opening porosity of 23.73%, hardness and flexural strength of 62 and 15.47MPa, from the fracture can be seen more porous and evenly distributed.

THE PREPARATION OF SiC POROUS CERAMIC PREFORMS

Preparation of Porous SiC Ceramic Using Bamboo Charcoal and Silica Sol As Pore-Forming Agents

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

PREPARATION AND CHARACTERIZATION OF SiC POROUS CERAMICS SUPPORT

Thermal Conductivity and Microstructure Properties of Porous SiC Ceramic Derived from Silicon Carbide Powder

Preparation and Properties of Porous Silicon Carbide Ceramics Through Coat-Mix and Composite Additives Process

Preparation of Porous SiC Ceramics Using Starch as Pore-forming Agent

Fabrication and Properties of SiC/mullite Composite Porous Ceramics

Effect of Activator on Properties of SiC Porous Ceramics

Effect of Sintering Temperature on Properties of Porous SiC Ceramics Produced Through Coat-mix/Composite Additives Process

Processing, Microstructures and Mechanical Properties of Aqueous Gelcasted and Solid-State-Sintered Porous Sic Ceramics

Microstructure Evolution Process of Porous Silicon Carbide Ceramics Prepared Through Coat-Mix Method

Preparation and Pore Structure Characteristics of SiC Honeycomb Ceramics with Macroporous Walls

Preparation and study of porous Si3N4 ceramics with high strength

Study on Preparation of SiC Preform for Electronic Packaging Material

Fabrication of Co-Continuous SiC/Al Composites from Novel SiC Preforms with High Porosity and Controllable Pore Size

Effects of Molding Temperature on Properties of Porous SiC Ceramics

Influence of Sintering Atmosphere on the Performance of Porous Silicon Carbide Ceramics

Microstructure Evolution and Performance Improvement of Silicon Carbide Ceramics via Impregnation Method

Effect of Al(OH)<sub>3</sub> Addition on the Properties of SiC/Al<sub>2</sub>O<sub>3</sub> Composite Porous Ceramics

Porous SiC Ceramics with Controllable Porosity Achieved by Micro-sized Powder through Recrystallization Sintering