Abstract:Silica samples condensed at acidic, neutral and alkaline media in the presence of various inorganic anions have been carefully investigated by 29Si MAS NMR spectroscopy. The results show that SO42- and CO32- could effectively improve the degree of silica condensation under neutral and alkaline media. Accordingly, for example, it is designable to synthesize hydrothermally stable and well ordered hexagonal mesoporous SBA-15 with very high degree of silica condensation in the presence of sulfate and carbonate species under neutral condition. As we expected, hexagonal mesoporous silica materials in the presence of sulfate (SBA-15-S) and carbonate species (SBA-15-U) show high degree of silica condensation, giving Q4/Q3 ratios at 6.3 and 4.3, which are much higher than that of conventional SBA-15 (Q4/(Q3+Q2) ratio at 1.8) synthesized in the absence of sulfate and carbonate species. Very interestingly, hexagonal mesoporous SBA-15-S and SBA-15-U shows very high hydrothermal stability, compared with SBA-15. For example, after being treated in 100% steaming at 780°C for 3h, SBA-15-S still remains its mesostructure. In constrast, SBA-15 loses most of the mesostructure. Furthermore, heteroatoms-substituted mesoporous materials such as aluminosilicate (Al-SBA-15-U) could also be synthesized in the presence of urea under neutral condition, and Al-SBA-15-U exhibits extraordinary hydrothermal stability. The unique and novel route for syntheses of hydrothermally stable and well ordered mesoporous silica and aluminosilicate materials in the presence of sulfate and carbonate species would be very important for potential application of mesoporous silica (SBA-15) and aluminosilicate materials (Al-SBA-15) as industrially supports and acidic catalysts.

Unusual Mesoporous Sba-15 With Parallel Channels Running Along The Short Axis

Alkanes-assisted Low Temperature Formation of Highly Ordered SBA-15 with Large Cylindrical Mesopores.

Preparation of Cross-Linked Bimodal Mesoporous SBA-15 with Numerous Pore Openings.

Fabrication of Three-Dimensional Large-Pore Mesoporous Channels Based on Ordered Mesoporous Silica Materials

Ordered hexagonal mesoporous silica materials (SBA-15) with additional disordered large-mesopore networks formed by gaseous expansion

One-step Direct Synthesis of Mesoporous Aluminosilicates Al-SBA-15 with Cage-Like Macropores by Using Micrometer-Sized Aluminum Balls

Synthesis of Highly Ordered Donut-Like Mesoporous Silica Sba-15

Creation Of Acid Sites On Sba-15 Mesoporous Silica By Alumination

Synthesis and Characterization of Small Pore Thick-Walled SBA-16 Templated by Oligomeric Surfactant with Ultra-Long Hydrophilic Chains

High-Surface-Area Zeolitic Silica with Mesoporosity

Triblock Copolymer Syntheses of Mesoporous Silica with Periodic 50 to 300 Angstrom Pores

Facile Synthesis of Crystal Like Shape Mesoporous Silica SBA-16

Morphological Control of Highly Ordered Mesoporous Silica Sba-15

Mesostructured Silica SBA-16 with Tailored Intrawall Porosity Part 1: Synthesis and Characterization

Modeling micelle-templated mesoporous material SBA-15: atomistic model and gas adsorption studies

Synthesis of Mesoporous Silica Single Crystal SBA-16 Assisted by Fluorinated Surfactants with Short Carbon-Chains

Mesotunnels on the Silica Wall of Ordered Sba-15 to Generate Three-Dimensional Large-Pore Mesoporous Networks

The Search of Promoters for Silica Condensation and Rational Synthesis of Hydrothermally Stable and Well Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at Conventional Temperature

SCM-25: A Zeolite with Ordered Meso-cavities Interconnected by 12 × 12 × 10-Ring Channels Determined by 3D Electron Diffraction

Three-Dimensional Cubic Mesoporous Structures of SBA-12 and Related Materials by Electron Crystallography

A simple method to directly synthesize Al-SBA-15 mesoporous materials with different Al contents