Abstract:Silica samples condensed at acidic, neutral and alkaline media in the presence of various inorganic anions have been carefully investigated by 29Si MAS NMR spectroscopy. The results show that SO42- and CO32- could effectively improve the degree of silica condensation under neutral and alkaline media. Accordingly, for example, it is designable to synthesize hydrothermally stable and well ordered hexagonal mesoporous SBA-15 with very high degree of silica condensation in the presence of sulfate and carbonate species under neutral condition. As we expected, hexagonal mesoporous silica materials in the presence of sulfate (SBA-15-S) and carbonate species (SBA-15-U) show high degree of silica condensation, giving Q4/Q3 ratios at 6.3 and 4.3, which are much higher than that of conventional SBA-15 (Q4/(Q3+Q2) ratio at 1.8) synthesized in the absence of sulfate and carbonate species. Very interestingly, hexagonal mesoporous SBA-15-S and SBA-15-U shows very high hydrothermal stability, compared with SBA-15. For example, after being treated in 100% steaming at 780°C for 3h, SBA-15-S still remains its mesostructure. In constrast, SBA-15 loses most of the mesostructure. Furthermore, heteroatoms-substituted mesoporous materials such as aluminosilicate (Al-SBA-15-U) could also be synthesized in the presence of urea under neutral condition, and Al-SBA-15-U exhibits extraordinary hydrothermal stability. The unique and novel route for syntheses of hydrothermally stable and well ordered mesoporous silica and aluminosilicate materials in the presence of sulfate and carbonate species would be very important for potential application of mesoporous silica (SBA-15) and aluminosilicate materials (Al-SBA-15) as industrially supports and acidic catalysts.

Facile Synthesis of Crystal Like Shape Mesoporous Silica SBA-16

Synthesis of Mesoporous Silica Single Crystal SBA-16 Assisted by Fluorinated Surfactants with Short Carbon-Chains

Synthesis of highly ordered large pore mesoporous silica SBA-16 spheres

Synthesis and Characterization of Small Pore Thick-Walled SBA-16 Templated by Oligomeric Surfactant with Ultra-Long Hydrophilic Chains

Preparation of Highly Ordered Well-Defined Single Crystal Cubic Mesoporous Silica Templated by Gemini Surfactant

Synthesis and characterization of Ti-SBA-16 ordered mesoporous silica composite

Facile synthesis of hierarchically mesoporous silica particles with controllable cavity in their surfaces.

A Facile Way to Synthesize Mesoporous Silica with Ia3d Cubic Symmetry

Synthesis of easily shaped ordered mesoporous titanium-containing silica

High-Surface-Area Zeolitic Silica with Mesoporosity

Synthesis of silica mesoporous crystals with controlled structure and morphology using gemini surfactant

The Search of Promoters for Silica Condensation and Rational Synthesis of Hydrothermally Stable and Well Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at Conventional Temperature

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Creation Of Acid Sites On Sba-15 Mesoporous Silica By Alumination

Novel Mesoporous Silicates with Two-Dimensional Mesostructure Direction Using Rigid Bolaform Surfactants

Facile synthesis of high quality mesoporous SBA-15 with enhanced control of the porous network connectivity and wall thickness

Control of Crystal Morphology of SBA-1 Mesoporous Silica

Synthesis and Morphology Control of Sba-1 Mesoporous Silica with Surfactant of Cetyltrimethylammonium Bromide (Ctmabr)

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Synthesis of Mesoporous Silica Single Crystal of Rhombic Dodecahedron Using Tri-head Group Quarternary Ammonium Cationic Surfactant

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions