Abstract:A family of highly ordered mesoporous (20-300 Angstrom) silica structures have been synthesized by the use of commercially available nonionic alkyl poly(ethylene oxide) (PEO) oligomeric surfactants and poly(alkylene oxide) block copolymers in acid media. Periodic arrangements of mescoscopically ordered pores with cubic 1m (3) over bar m, cubic Pm (3) over bar m (or others), 3-d hexagonal (P6(3)/mmc), 2-d hexagonal (p6mm), and lamellar (L-alpha) symmetries have been prepared. Under acidic conditions at room temperature, the nonionic oligomeric surfactants frequently form cubic or 3-d hexagonal mesoporous silica structures, while the nonionic triblock copolymers tend to form hexagonal (p6mm) mesoporous silica structures. A cubic mesoporous silica structure (SBA-11) with Pm (3) over bar m diffraction symmetry has been synthesized in the presence of C16H33(OCH2CH2)(10)OH (C16EO10) surfactant species, while a 3-d hexagonal (P6(3)/mmc) mesoporous silica structure (SBA-12) results when C18EO10 is used. Surfactants with short EO segments tend to form lamellar mesostructured silica at room temperature. Hexagonal mesoporous silica structures with d(100) spacings of 64-77 Angstrom can be synthesized at 100 degrees C by using oligomeric nonionic surfactants. Highly ordered hexagonal mesoporous silica structures (SBA-15) with unusually large d(100) spacings of 104-320 A have been synthesized in the presence of triblock poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO) copolymers. SBA-15 mesoporous structures have been prepared with BET surface areas of 690-1040 m(2)/g, pore sizes of 46-300 Angstrom, silica wall thicknesses of 31-64 Angstrom, and pore volumes as large as 2.5 cm(3)/g. A novel cubic (Im (3) over bar m) cage-structured mesoporous silica structure (SBA-16) with a large cell parameter (a = 176 ii) has been synthesized using triblock copolymers with large PEO segments. The EO/PO ratio of the copolymers can be used to control the formation of the silica mesophase: lowering this ratio of the triblock copolymer moieties promotes the formation of lamellar mesostructured silica, while higher ratios favor cubic mesostructured silica. Cubic mesoporous structures are also obtained when star diblock copolymers are used as structure-directing agents. The calcined ordered mesoporous silicas reported in this paper an thermally stable in boiling water for at least 48 h. The assembly of the inorganic and organic periodic composite materials appears to lake place by a hydrogen bonding (S-0 H+)(X-I+) pathway. The assembly race r increases with increasing concentration of [H+] and [Cl-], according to the kinetic expression r = k[H+](0.31)[Cl-](0.31).

Synthesis of Highly Ordered Donut-Like Mesoporous Silica Sba-15

Morphological Control of Highly Ordered Mesoporous Silica Sba-15

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Ordered hexagonal mesoporous silica materials (SBA-15) with additional disordered large-mesopore networks formed by gaseous expansion

Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

Synthesis of Highly Ordered Large-pore Mesoporous Organosilicas by Non-aqueous Solvent Evaporation Method

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Triblock Copolymer Syntheses of Mesoporous Silica with Periodic 50 to 300 Angstrom Pores

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions

Anionic Surfactant Induced Mesophase Transformation to Synthesize Highly Ordered Large-Pore Mesoporous Silica Structures

Alkanes-assisted Low Temperature Formation of Highly Ordered SBA-15 with Large Cylindrical Mesopores.

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Synthesis of Ordered Mesoporous Silica Spheres with Controllable Diameter in Micrometer

Ordered cubic mesoporous silicas with large pore sizes synthesized via high-temperature route.

Semi-fluorinated Surfactant Syntheses of Ordered Porous Materials with Tailorable Pore Sizes

Synthesis of Mesoporous Silica with A Three-Dimensional Hexagonal Ordered Structure Using Cationic and Amphoteric Mixed Surfactants

Ordered bimodal mesoporous silica with tunable pore structure and morphology

The Search of Promoters for Silica Condensation and Rational Synthesis of Hydrothermally Stable and Well Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at Conventional Temperature

Novel Mesoporous Silicates with Two-Dimensional Mesostructure Direction Using Rigid Bolaform Surfactants