Morphological Control of Highly Ordered Mesoporous Silica Sba-15

DY Zhao,JY Sun,QZ Li,GD Stucky

DOI: https://doi.org/10.1021/cm9911363

IF: 10.508

2000-01-01

Chemistry of Materials

Abstract:Highly ordered hexagonal mesoporous silica SEA-15 with fiber, rope, donut, sphere, gyroid, and discoid-like morphology have been synthesized.

What problem does this paper attempt to address?

Synthesis of Highly Ordered Donut-Like Mesoporous Silica Sba-15

JY Sun,DY Zhao

DOI: https://doi.org/10.3321/j.issn:0251-0790.2000.01.031

2000-01-01

Abstract:Highly ordered hexagonal mesoporous silica SEA-15 with tunable morphology such as donut-like has been synthesized through the cosolvent approach. Donut-like SEA-15 prepared by using DMF cosolvent shows highly ordered circle channels and large mesopore size of 9.9 nm and pore volume of 1.45 cm(3)/g. Cosurfactant approach has also been used to control the morphology of SEA-15, resulting that highly ordered hard spheres (uniformed diameter-800 nm) mesoporous silica are formed. The morphology of mesoporous SEA-15 is much depended on the surface curvature energy of interface of inorganic silica and organic block copolymer species.
Morphological control of highly ordered mesoporous carbon

C. Yu,J. Fan,B. Tian,F. Zhang,G.D. Stucky,D. Zhao

DOI: https://doi.org/10.1016/S0167-2991(03)80323-3

2003-01-01

Abstract:Highly ordered mesoporous carbon materials with fiber-like, plate-like, rod-like and donut-like morphologies have been synthesized by using mesoporous silica as the templates.
Control of morphology in synthesizing mesoporous silica

Chung-Yuan Mou,Hong-Ping Lin

DOI: https://doi.org/10.1351/pac200072010137

2000-01-01

Pure and Applied Chemistry

Abstract:Abstract Mesoporous silica can be synthesized by either the alkaline route or the acidic route, both using surfactants as templates. Morphological transformations of mesoporous silica can produce various hierarchical orders. Different morphologies are produced under different synthetic conditions. In the alkaline route, the surfactant/silicate liquid crystal system undergoes phase transformation to form vesicles and further transforms to the hexagonal phase. The results are tubule-within-tubule and hollow pillar-within-sphere structures depending on cosurfactant/surfactant composition. Using nitric acid in the acidic route, one can obtain hierarchical ropes or gyroids depending on stirring conditions. Ammonia hydrothermal treatment can induce further morphological transformation to nanotubes of mesoporous silica.

chemistry, multidisciplinary
Novel Mesoporous Silicates with Two-Dimensional Mesostructure Direction Using Rigid Bolaform Surfactants

Dongyuan Zhao,Qisheng Huo,Jianglin Feng,Jiman Kim,Yongjin Han,Galen D. Stucky

DOI: https://doi.org/10.1021/cm980755t

IF: 10.508

1999-01-01

Chemistry of Materials

Abstract:In this paper we describe how pore-structure modification can be achieved in a highly ordered fashion through the use of bolaform surfactants containing a rigid unit in the hydrophobic chain. The silicate mesophase, SBA-8, synthesized using bolaform surfactants at room temperature, is a two-dimensional (2-D) pore structure with a centered rectangular lattice (space group cmm, 1 < a/b < root 3), which has no reported lyotropic liquid crystal analogue. SBA-8 is thermally stable in air, and the surfactant can be removed by calcination to yield a mesoporous material with a high surface area(>1000 m(2)/g), The unit cell parameter of the silicate mesostructure can be varied by adding gemini surfactants or by changing reaction temperature; a 2-D silicate mesophase (M alpha, a/b > root 3) and high quality hexagonal MCM-41 (p6mm, a/b = root 3) can be obtained. Hydrothermal transformation of SBA-8 into MCM-41 takes place, confirming the intermediate nature of the SBA-8 mesophase.
Synthesis and Morphology Control of Sba-1 Mesoporous Silica with Surfactant of Cetyltrimethylammonium Bromide (Ctmabr)

S Che,Y Sakamoto,O Terasaki,T Tatsumi

DOI: https://doi.org/10.1246/cl.2002.214

2002-01-01

Chemistry Letters

Abstract:The 3d-cubic Pm3-n SBA-1 mesoporous silica synthesized under highly acidic conditions using cetyltrimethylammonium bromide exhibited a distinct octadecahedron crystal shape in contrast to the material synthesized in the presence of cetyltriethylammonium bromide under less acidic conditions, which showed a highly isotropic morphology with fifty-four or more crystal faces.
Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Defeng Li,Xiangyu Guan,Jiangwei Song,Yan Di,Daliang Zhang,Xin Ge,Lan Zhao,Feng-Shou Xiao

DOI: https://doi.org/10.1016/j.colsurfa.2005.07.027

2006-01-01

Abstract:Ordered mesoporous silica materials (SBA-family) with 2-D hexagonal (p6mm) and 3-D cubic (Im3m) symmetry have been efficiently synthesized by using the mixture of triblock copolymer surfactant and sodium dodecylsulfonate as co-templates at relatively low concentration. X-ray diffraction (XRD), transmission electron microscopy (TEM), and nitrogen adsorption/desorption isotherms are used to characterize these mesoporous silica materials, and the results show that the mesoporous silica mateials synthesized from the mixed surfactants have better mesostructural order and smaller mesopore size, compared with mesoporous silica materials of SBA-15 and SBA-16. Moreover, the microporosity in these ordered mesoporous materials is well controlled by the weight ratios of polymer surfactant to anionic surfactant. Particularly, when P123 concentration in the starting gel is reduced to less than 0.4wt.%, the walls of ordered hexagonal mesoporous silica are micropore-free.
Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

Dongyuan Zhao,Qisheng Huo,Jianglin Feng,Bradley F. Chmelka,Galen D. Stucky

DOI: https://doi.org/10.1021/ja974025i

IF: 15

1998-01-01

Journal of the American Chemical Society

Abstract:A family of highly ordered mesoporous (20-300 Angstrom) silica structures have been synthesized by the use of commercially available nonionic alkyl poly(ethylene oxide) (PEO) oligomeric surfactants and poly(alkylene oxide) block copolymers in acid media. Periodic arrangements of mescoscopically ordered pores with cubic 1m (3) over bar m, cubic Pm (3) over bar m (or others), 3-d hexagonal (P6(3)/mmc), 2-d hexagonal (p6mm), and lamellar (L-alpha) symmetries have been prepared. Under acidic conditions at room temperature, the nonionic oligomeric surfactants frequently form cubic or 3-d hexagonal mesoporous silica structures, while the nonionic triblock copolymers tend to form hexagonal (p6mm) mesoporous silica structures. A cubic mesoporous silica structure (SBA-11) with Pm (3) over bar m diffraction symmetry has been synthesized in the presence of C16H33(OCH2CH2)(10)OH (C16EO10) surfactant species, while a 3-d hexagonal (P6(3)/mmc) mesoporous silica structure (SBA-12) results when C18EO10 is used. Surfactants with short EO segments tend to form lamellar mesostructured silica at room temperature. Hexagonal mesoporous silica structures with d(100) spacings of 64-77 Angstrom can be synthesized at 100 degrees C by using oligomeric nonionic surfactants. Highly ordered hexagonal mesoporous silica structures (SBA-15) with unusually large d(100) spacings of 104-320 A have been synthesized in the presence of triblock poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO) copolymers. SBA-15 mesoporous structures have been prepared with BET surface areas of 690-1040 m(2)/g, pore sizes of 46-300 Angstrom, silica wall thicknesses of 31-64 Angstrom, and pore volumes as large as 2.5 cm(3)/g. A novel cubic (Im (3) over bar m) cage-structured mesoporous silica structure (SBA-16) with a large cell parameter (a = 176 ii) has been synthesized using triblock copolymers with large PEO segments. The EO/PO ratio of the copolymers can be used to control the formation of the silica mesophase: lowering this ratio of the triblock copolymer moieties promotes the formation of lamellar mesostructured silica, while higher ratios favor cubic mesostructured silica. Cubic mesoporous structures are also obtained when star diblock copolymers are used as structure-directing agents. The calcined ordered mesoporous silicas reported in this paper an thermally stable in boiling water for at least 48 h. The assembly of the inorganic and organic periodic composite materials appears to lake place by a hydrogen bonding (S-0 H+)(X-I+) pathway. The assembly race r increases with increasing concentration of [H+] and [Cl-], according to the kinetic expression r = k[H+](0.31)[Cl-](0.31).
Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Xiqing Wang,Yu Zhang,Wei Luo,Ahmed A. Elzatahry,Xiaowei Cheng,Abdulaziz Alghamdi,Aboubakr M. Abdullah,Yonghui Deng,Dongyuan Zhao

DOI: https://doi.org/10.1021/acs.chemmater.6b00499

IF: 10.508

2016-01-01

Chemistry of Materials

Abstract:A facile nonpolar solvent-assisted Stober method has been developed to synthesize ordered mesoporous silica materials with tunable pore size and diverse morphologies and mesostructures by using cetyltrimethylammonium bromide as the template and tetraethyl orthosilicate as silica precursor in a simple aqueous-phase synthesis system. By simply changing the amount of n-hexane and ammonia-water in the system, ordered mesoporous silica with pore sizes of 2.7-10.5 nm, various morphologies (nanocubes, truncated nanocubes, core-shell microspheres, and twisted nanorods), a high surface area up to 888 m(2)/g, and a large pore volume of 1.55 cm(3)/g are synthesized. Owing to their highly hydrophilic surface, large and accessible pores, and high surface area, the mesoporous silica materials exhibit an excellent performance in adsorption of dye molecules of large dimension (1.6 nm) with a maximum adsorption capacity of 106 mg/g in 10 min at 200 mg/L initial Rhodamine B concentration.
Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

DH Chen,Z Li,CZ Yu,YF Shi,ZD Zhang,B Tu,DY Zhao

DOI: https://doi.org/10.1021/cm050209h

IF: 10.508

2005-01-01

Chemistry of Materials

Abstract:Mesoporous silica with Ia (3) over bard structure has been successfully prepared by using mixed surfactants of commercially available nonionic block copolymer P123 (EO(20)PO(70)EO(20)) and anionic sodium dodecyl sulfate (SDS) as structure-directing agents through an acid-catalyzed silica sol-gel process. XRD, TEM, and N(2) sorption measurements show that the products have highly ordered bicontinuous cubic mesostructure with high surface area (similar to 770 m(2)/g), large pore volume (similar to 1.5 cm(3)/g) and uniform pore size (similar to 10 nm). Effects of preparation parameters on the formation of the mesostructure have been extensively investigated. It is found that the molar ratios of SDS/P123 between 2.1 and 2.5 and that of silicic species to P123 in the range from 40 to 75 are favorable for the formation of highly ordered Ia (3) over bard mesostructure. Prolonging hydrothermal treatment time leads to almost unchanged cell parameters of the products, whereas there is obvious increase of the pore sizes and pore volume. The results show that resultant template-free mesoporous silica products have excellent thermal stability, and they are more stable in N2 atmosphere than in air. Morphologies of the resultant materials can be further controlled by adding inorganic salt (such as Na(2)SO(4)) into the mixed surfactants system. Coral- and petaline-like mesoporous silica with continuous skeletons can be obtained. Understanding this synthesis system might be useful for economical and large-scale production of mesoporous materials with controllable structures.
Polymorphism of Silica Mesostructures Templated by Poly(Ethylene Oxide)-b-Poly(Butylene Oxide) Diblock Copolymer

Yonghao Yu,Chengzhong Yu,Yú Zhang,Dongyuan Zhao

DOI: https://doi.org/10.1246/cl.2000.504

2000-01-01

Chemistry Letters

Abstract:A family of silica mesostructures including highly ordered 2-dimensional (2D) hexagonal (H1) and lamellar (Lα) symmetries have been prepared by using poly(ethylene oxide)-poly(butylene oxide) diblock copolymer as a structure-directing agent under acidic synthesis condition.
Highly ordered mesoporous silica structures templated by poly(butylene oxide) segment di- and tri-block copolymers

Chengzhong Yu,Yonghao Yu,Lei Miao,Dongyuan Zhao

DOI: https://doi.org/10.1016/S1387-1811(01)00169-X

IF: 5.876

2001-01-01

Microporous and Mesoporous Materials

Abstract:Highly ordered mesoporous silica structures including body-centered cubic (Im3m), two-dimensional hexagonal (p6mm) and lamellar (Lα) symmetries have been synthesized by using hydrophobic poly(butylene oxide) moiety diblock and triblock copolymers as structure-directing agents. Under acidic condition, highly ordered, caged cubic mesoporous silica structures (FDU-1, Im3m) with a large cell parameter (a=220Å) can be formed in the presence of triblock poly(ethylene oxide)–poly(butylene oxide)–poly(ethylene oxide) (PEO–PBO–PEO) copolymer such as EO39BO47EO39. Calcined FDU-1 has a largest pore size of 120 Å among all known cubic silica mesostructures, a pore volume of 0.77 cm3/g, and a BET surface area of 740 m2/g. Diblock poly(butylene oxide)–poly (ethylene oxide) (PBO–PEO) copolymer such as BO10EO16 favors to yield highly ordered two-dimensional hexagonal (p6mm) silica mesostructures with a well-uniformed pore size of 60 Å and a large BET surface area of 902 m2/g. Lamellar (Lα) mesostructures can also be obtained when high concentration diblock copolymer is used as the structure-directing agent. The calcined cubic mesostructured silica FDU-1 is hydrothermally stable in boiling water for at least nine days.
Morphology Development of Mesoporous Materials: A Colloidal Phase Separation Mechanism

Chengzhong Yu,Jie Fan,Bozhi Tian,Dongyuan Zhao

DOI: https://doi.org/10.1021/cm035011g

IF: 10.508

2004-01-01

Chemistry of Materials

Abstract:Synthetic conditions such as temperature, stirring rate, ionic strength, acidity, and reactant ratios that affect the mesostructures and macrostructures of mesoporous materials have been extensively studied in the nonionic block copolymer templating system. Highly ordered SBA-15 materials with similar to100% rodlike morphologies (similar to1-2 mum long) have been obtained in the presence of inorganic salts. Synthesis conditions such as low temperature, low acidity, and low ionic strength that increase the induction time give rise to the morphologies of mesoporous silica with increased curvatures. The particle growth process of rodlike SBA-15 materials from solutions has been examined by directly observing the morphologies of particles as a function of time. A colloidal phase separation mechanism (CPSM) for the formation of mesoporous materials is proposed. It is suggested that the formation process of mesoporous materials involves three stages: (1) cooperative self-assembly of inorganic/organic composites; (2) formation of a new crystal-like phase rich in aggregates of block copolymer/silica species; and (3) phase separation of this liquid crystal-like phase from the solution and further growth of solid mesostructures driven by further condensation of silica species. The morphologies of mesoporous materials are developed after the phase separation stage and influenced by the competition mainly between the free energy of mesostructure self-assembly (DeltaG) and the colloidal surface free energy (F), as well as other interactions such as the shearing force. When the phase separation stage occurs early, DeltaG is dominant and the macrostructure of mesoporous materials is developed together with the formation of mesostructure; therefore, mesoporous materials with crystal-like morphologies can be generated. The role of inorganic salts is well explained based on the CPSM by taking into account the colloidal interaction enhanced by inorganic salts. Cubic (Im (3) over barm) mesoporous single crystals have been obtained with exclusively rhombdodecahedron shapes (1-2 mum in size). Ultrathin microtoming TEM measurements confirm that such polyhedral particles are perfect single crystals. The different influences of hydrothermal treatments upon the mesostructures and macrostructures have been discussed in the hexagonal and cubic synthesis systems. By employing the CPSM, hexagonal mesoporous single crystals have been obtained in the absence of inorganic salts; the size limitation (similar to1-2 mum) of mesoporous single crystals has also been discussed. Such understandings may be useful in the fabrication of mesoporous materials with well-defined, crystal-like morphologies.
Highly Ordered Large Caged Cubic Mesoporous Silica Structures Templated by Triblock PEO–PBO–PEO Copolymer

CZ Yu,YH Yu,DY Zhao

DOI: https://doi.org/10.1039/b000603n

IF: 4.9

2000-01-01

Chemical Communications

Abstract:Highly ordered, hydrothermally stable, caged cubic mesoporous silica structures (Im(3) over bar m) with unusually large pore size (120 Angstrom) have been synthesized by using hydrophobic poly(butylene oxide) containing triblock PEO-PBO-PEO copolymer as a structure-directing agent.
Highly ordered cubic mesoporous materials with the same symmetry but tunable pore structures.

Chengzhong Yu,J. Zou,Jie Yang,Xiaojun Bao,P. Yuan,Dongyuan Zhao

DOI: https://doi.org/10.1021/la303187d

IF: 3.9

2012-11-14

Langmuir

Abstract:In this article, two highly ordered mesoporous silica materials with the same face-centered cubic (fcc) symmetry but distinctly different pore structures have been synthesized by simply changing the amount of silica source. Their structures have been extensively studied by Synchrotron small-angle X-ray scattering, N(2) sorption analysis, scanning and transmission electron microscopy observations, and electron tomography. One mesoporous material formed by a hard sphere packing (HSP) pathway exhibits a bimodal pore distribution, while the other has a conventional FDU-12-type mesostructure with a single-sized pore. By increasing the amount of the silica source, the cavities formed by the packing of composite spherical micelles in the HSP mesostructure are gradually filled by the excess of siliceous species, leading to the conventional FDU-12-type mesostructure with the disappearance of bimodal pores. The pore connectivity of the HSP mesoporous material hydrothermally treated at 150 °C has been further investigated. Taking advantage of the ultrathin tomographic slices, the sizes of cage, cavity, and connectivity are measured to be 14.5, 10.5, and 6.4 nm, respectively. More importantly, the pore connection between the cage and cavity is directly observed to occur along the ⟨100⟩ direction, different from the FDU-12-type mesostructure in which the connection appears between two adjacent cages along the ⟨110⟩ direction. This work represents an unusual example where two ordered cage-type mesoporous materials with the same symmetry can be synthesized by slightly changing the synthesis condition, but their pore structures and pore connections are significantly different. Our finding is important for understanding the formation mechanism and for the rational design and controllable synthesis of novel mesoporous materials.

Medicine,Materials Science
Synthesis of highly ordered large pore mesoporous silica SBA-16 spheres

Hongxiao Jin,Qingyin Wu,Chao Chen,Daliang Zhang,Wenqin Pang

DOI: https://doi.org/10.1016/S0167-2991(07)80396-X

2007-01-01

Abstract:null
Supramolecular-Templating Synthesis of Mesoporous Silica: Control of Structure and Morphology

YR Ma,LM Qi,JM Ma

2003-01-01

Progress in chemistry

Abstract:The recent progress in the supramolecular-templating synthesis of ordered mesoporous silica has been reviewed. The discussion is focused on the control of the internal structure (the mesostructure and the related structural parameters) and exterior morphology of the mesoporous silica templated by both cationic surfactants and poly(ethylene oxide) based block copolymers. The potential development of the research on mesoporous silica is also proposed.
Control of Morphology and Helicity of Chiral Mesoporous Silica

H. Jin,Z. Liu,T. Ohsuna,O. Terasaki,Y. Inoue,K. Sakamoto,T. Nakanishi,K. Ariga,S. Che

DOI: https://doi.org/10.1002/adma.200502038

IF: 29.4

2006-01-01

Advanced Materials

Abstract:Chiral ordered mesoporous silica has been synthesized by using a chiral surfactant (N-myristoyl-L-alanine sodium salt) as a template, 3-aminopropyl-triethoxysilane as a co-structure directing agent, and tetraethoxylsilane as an inorganic source. The helicity and the morphology of the mesoporous silica are determined by the stirring rate during the chiral surfactant self-assembly (see Figure), providing new insight into the chiral self-assembly of molecules.
Triblock Copolymer Syntheses of Mesoporous Silica with Periodic 50 to 300 Angstrom Pores

DY Zhao,JL Feng,QS Huo,N Melosh,GH Fredrickson,BF Chmelka,GD Stucky

DOI: https://doi.org/10.1126/science.279.5350.548

IF: 56.9

1998-01-01

Science

Abstract:Use of amphiphilic triblock copolymers to direct the organization of polymerizing silica species has resulted in the preparation of well-ordered hexagonal mesoporous silica structures (SBA-15) with uniform pore sizes up to approximately 300 angstroms. The SBA-15 materials are synthesized in acidic media to produce highly ordered, two-dimensional hexagonal (space group p6mm) silica-block copolymer mesophases. Calcination at 500 degrees C gives porous structures with unusually large interlattice d spacings of 74.5 to 320 angstroms between the (100) planes, pore sizes from 46 to 300 angstroms, pore volume fractions up to 0.85, and silica wall thicknesses of 31 to 64 angstroms. SBA-15 can be readily prepared over a wide range of uniform pore sizes and pore wall thicknesses at low temperature (35 degrees to 80 degrees C), using a variety of poly(alkylene oxide) triblock copolymers and by the addition of cosolvent organic molecules. The block copolymer species can be recovered for reuse by solvent extraction with ethanol or removed by heating at 140 degrees C for 3 hours, in both cases, yielding a product that is thermally stable in boiling water.
Novel Mesoporous ZSM-5 Zeolite with Disparate Morphologies Synthesized by a Double Long-alkyl-chain Organosilane Template

Fei Zhao,Dongliang Liu,Yijiang Wang

DOI: https://doi.org/10.3139/113.110478

2017-01-01

Abstract:A novel hierarchical ZSM-5 zeolite containing two disparate morphologies was prepared by using a new organosilane surfactant with two long alkyl chains. Main crystal phase arrayed regularly and stacked in dense layers. However, the rest of crystalline phase was shaped like egg tarts.
Mesoporous Materials with Spherical Morphology: Synthesis and Bioapplication

HF Yang,Y Yan,DY Zhao

IF: 6.76

2004-01-01

Journal of Industrial and Engineering Chemistry

Abstract:Morphology control is one of the most interesting issues in the research field of mesoporous materials. It plays a very important role in understanding the basic synthesis mechanism of the kind of materials. Moreover, the future applications of mesoporous materials are strongly depended on their tunable macroscopical morphologies. Mesoporous materials with spherical morphology are quite attractive due to the potential applications in macromolecular separations, drug deliveries, catalysis supports and template agents for photonic crystals. Researches on synthesis and properties of the materials have been carried out for nearly ten years. In this article, several synthetic methods for both siliceous and non-siliceous mesoporous spheres are reviewed, including solution self-assembly, aerosol spraying and hard templating route. The mechanism of self-assembly in solution system is provided and the rational controls for synthetic conditions are specifically discussed. With the viewpoint of applications, some examples are given in the aspects of bioseparations, drug delivery and catalysis. A short summary has listed some overviews for future developments.

Morphological Control of Highly Ordered Mesoporous Silica Sba-15

Synthesis of Highly Ordered Donut-Like Mesoporous Silica Sba-15

Morphological control of highly ordered mesoporous carbon

Control of morphology in synthesizing mesoporous silica

Novel Mesoporous Silicates with Two-Dimensional Mesostructure Direction Using Rigid Bolaform Surfactants

Synthesis and Morphology Control of Sba-1 Mesoporous Silica with Surfactant of Cetyltrimethylammonium Bromide (Ctmabr)

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Polymorphism of Silica Mesostructures Templated by Poly(Ethylene Oxide)-b-Poly(Butylene Oxide) Diblock Copolymer

Highly ordered mesoporous silica structures templated by poly(butylene oxide) segment di- and tri-block copolymers

Morphology Development of Mesoporous Materials: A Colloidal Phase Separation Mechanism

Highly Ordered Large Caged Cubic Mesoporous Silica Structures Templated by Triblock PEO–PBO–PEO Copolymer

Highly ordered cubic mesoporous materials with the same symmetry but tunable pore structures.

Synthesis of highly ordered large pore mesoporous silica SBA-16 spheres

Supramolecular-Templating Synthesis of Mesoporous Silica: Control of Structure and Morphology

Control of Morphology and Helicity of Chiral Mesoporous Silica

Triblock Copolymer Syntheses of Mesoporous Silica with Periodic 50 to 300 Angstrom Pores

Novel Mesoporous ZSM-5 Zeolite with Disparate Morphologies Synthesized by a Double Long-alkyl-chain Organosilane Template

Mesoporous Materials with Spherical Morphology: Synthesis and Bioapplication