Abstract:Lignite is widely used as the fuel for coal-fired power plants, and its flue gas temperature is about 50-100 degrees C higher than others. V2O5-WO3/TiO2 is extremely restricted in the selective catalytic reduction (SCR) of NO from the coal-fired power plants burning lignite due to the drop of NOx conversion, low N-2 selectivity, and volatility of vanadium pentoxide at high temperatures. Therefore, a more environmental-friendly SCR catalyst with excellent SCR activity and better N-2 selectivity at 350-450 degrees C should be developed for this application. In this work, sulfated Fe-Ti spinel catalyst was developed for the SCR of NO from the coal-fired power plants burning lignite. The drop of NOx conversion at high temperatures was mainly related to the simultaneous occurrence of the catalytic oxidization of NH3 to NO during the SCR reaction. Ti was incorporated into gamma-Fe2O3 to decease the oxidization ability of Fe3+ on the surface, and the sites for -NH2 adsorption and the active components for -NH2 oxidization were separated after the sulfation to decrease the probability of the collision between -NH2 adsorbed and Fe3+ on the surface. They both inhibited the catalytic oxidization of NH3 to NO over gamma-Fe2O3. However, the SCR reaction over gamma-Fe2O3 was simultaneously restrained after the incorporation Ti and the sulfation. Therefore, NOx conversion over gamma-Fe2O3 at high temperatures depended on the ratio of NH3 conversion through the catalytic oxidization of NH3 to NO to that through the SCR reaction. This ratio decreased after the incorporation of Ti, and it further decreased after the sulfation, resulting in an obvious promotion of NOx conversion at high temperatures. Therefore, sulfated Fe-Ti spinel showed excellent SCR activity, N-2 selectivity, and H2O+SO2 durability at 300-450 degrees C, which was suitable for the application in the coal-fired power plants burning lignite.

Selective catalytic reduction of NO by ammonia with fly ash catalyst☆

The development of Fe2O3-based catalysts used for the selective catalytic reduction of NOx with NH3: A review

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

The development of Fe2O3-based catalysts used for the selective catalytic reduction of NO with NH3: A review

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Substitution of WO3in V2O5/WO3–TiO2by Fe2O3for Selective Catalytic Reduction of NO with NH3

Fe And/or Mn Oxides Supported on Fly Ash-Derived SBA-15 for Low-Temperature NH3-SCR

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Iron oxide-based catalysts for low-temperature selective catalytic reduction of NOx with NH3

Iron Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOxwith NH3

Selective Catalytic Reduction of NO with NH3 over Mn–Fe/USY under Lean Burn Conditions

Low Temperature Selective Catalytic Reduction of NO and NO2 with NH3 over Activated Carbon-Supported Vanadium Oxide Catalyst

Improvement of the Activity of Γ-Fe2o3 for the Selective Catalytic Reduction of NO with NH3 at High Temperatures: NO Reduction Versus NH3 Oxidization

Highly dispersed MnOx-FeO(x)supported by silicalite-1 for the selective catalytic reduction of NO(x)with NH(3)at low temperatures

Capability of molecular sieve-supported FeSO_4 catalyst for selective catalytic reduction of NO_x

Micro-structured Cu-ZSM-5 catalyst on aluminum microfibers for selective catalytic reduction of NO by ammonia

Gd-Mn-Ti Composite Oxides Anchored on Waste Coal Fly Ash for the Low-Temperature Catalytic Reduction of Nitrogen Oxide

Performance of Fe-ZSM-5 for Selective Catalytic Reduction of NO X with NH 3 : Effect of the Atmosphere During the Preparation of Catalysts

High-performance Fe-Cu composite oxide for selective catalytic reduction of NO with NH3: Driving of Cu on α-Fe2O3

In-situ DRIFTS Investigation on the Selective Catalytic Reduction of NO with NH3 over the Sintered Ore Catalyst