Abstract:Bioceramic hydroxyapatite/sodium titanate coating on sandblasted titanium substrate was fabricated by a three-step process. At first, the sandblasted titanium substrate was coated with a flake-like sodium titanate layer by alkali-heat treatment. In the second step, the alkali-heat treated titanium substrate was hydrothermal treated at 180 °C for 4 h with calcium solutions. In the third step, the hydroxyapatite (HA) coating was deposited onto the hydrothermal treated layer via electrochemical deposition method. The surface topography and roughness of the coatings were determined by field emission scanning electron microscope (FESEM) and a mechanical contact profilometer, respectively. The surface compositions were evaluated by X-ray diffraction (XRD), energy-dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). The EDS, XPS, and XRD analysis confirm the presence of element Ca, Ca2+, and CaTiO3 on sodium titanate layer after hydrothermal treatment with Ca(NO3)2 solution, respectively. FESEM micrograph shows the rod/needle-shaped crystallites are highly densely packed on the calcium-ion-containing layer with an average size of ~50 nm in diameter. The results indicate that the sodium titanate layer containing Ca2+ ions possesses higher ability to induce HA formation compared with the pure sodium titanate layer. It is revealed that surface composition plays an important role in the electrochemical deposition of HA. The calcium-ion-containing layer probably makes the nucleation of HA easy and effectively promotes orientated growth of HA on flake-like sodium titanate surface. The sodium titanate layer possesses a lower corrosion current density and a higher corrosion potential than sandblasted-Ti substrate. The sodium titanate layer should act as a barrier to the release of metal ions from metallic substrate to physiological solutions and thus reducing the electrochemical reaction rate.

Fast deposition of hydroxyapatite coating on titanium alloy by a two-step acid-alkali treatment

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

Preparation of hydroxyapatite coating on smooth implant surface by electrodeposition

Effect of Supersaturation on the Morphology of Hydroxyapatite Crystals Deposited by Electrochemical Deposition on Titanium

Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Biomimetic Deposition of Hydroxyapatite by Mixed Acid Treatment of Titanium Surfaces

Hydroxyapatite coating on Ti6Al4V alloy using a sol–gel derived precursor

Hydroxyapatite Coating On Ti6a14v Alloy Using A Sol-Gel Derived Precursor

Hydrothermal treatment of Ti surface to enhance the formation of low crystalline hydroxyl carbonate apatite

Preparation and biological evaluation of Nano-HA coating on tatinium surfaces

One-step Modification of Nano-Hydroxyapatite Coating on Titanium Surface by Hydrothermal Method

Preparation of Layered Bioceramic Hydroxyapatite/Sodium Titanate Coatings on Titanium Substrates Using A Hybrid Technique of Alkali-Heat Treatment and Electrochemical Deposition

Preparation of Bioactive Hydroxyapatite on Pure Titanium

Electrohydrodynamic Coating of Metal with Nano-Sized Hydroxyapatite.

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Preparation of Dicalcium Phosphate Anhydrous (Monetite) Biological Coating on Titanium by Spray-Drying Method

Hydroxyapatite based on Abalone Mussel Shells Coating on Titanium Alloy using Electrophoretic Deposition Dip Coating as a Bone Implant Candidate

Carbonate apatite coating on titanium induced rapidly by precalcification.

Synthesis of Hydroxyapatite Coatings with Hexagonal Crystal Structure on Etched Titanium by Hydrothermal Method