Effect of Ni Coated SiC on Mechanical Properties of SiC/Fe Composites
bin bin wang,bing bing fan,wen li,chen yang wang,bing sun,biao zhao,xiao xuan pian,hao chen,rui zhang
DOI: https://doi.org/10.4028/www.scientific.net/KEM.602-603.578
2014-01-01
Key Engineering Materials
Abstract:A facile one-step in situ chemical deposition method was introduced to synthesize Ni coated SiC composite powders, which used NiCl2 center dot 6H(2)O as nickel source and N2H4 center dot H2O as reductant, respectively. SiC(Ni)/Fe composites were prepared by current-vacuum hot-pressed sintering at 850 degrees C, 40MPa for 30min. Scanning electronic microscope (SEM) and X-ray diffraction (XRD) were used to characterize the structure, morphology and composition of the prepared Ni/SiC core/shell composite powders. It is found that the Ni coated SiC is favorable to improve the dispersion and compatibility of SiC(Ni)/Fe composites. By a series of contrast experiments, it is shown that the sintering sample with 5wt% of SiC(Ni) has the best mechanical properties. The relative density, Vickers hardness and bending strength is 91.67%, 4.72GPa and 508MPa, respectively.