Lithium Selective Adsorption on 1-D MnO2 Nanostructure Ion-Sieve

Qin-Hui Zhang,Shao-Peng Li,Shu-Ying Sun,Xian-Sheng Yin,Jian-Guo Yu

DOI: https://doi.org/10.1016/j.apt.2009.02.008

IF: 4.969

2009-01-01

Advanced Powder Technology

Abstract:β-MnO2, spinel-type Li4Mn5O12 and pure cubic phase MnO2 nanorod, with the size about 20–140nm in diameter and 0.8–4μm in length, were synthesized via a combination of hydrothermal synthesis and low temperature solid-phase reaction, more favorable to control the nanocrystalline structure with well-defined pore size distribution and high surface area than the traditional high temperature calcination process. Further, the MnO2 ion-sieves with lithium selective adsorption property were prepared by the acid treatment process to completely extract lithium from the spinel Li4Mn5O12 precursor with little change to the Mn–O lattice structure and the 1-D nanorod morphology. The effects of hydrothermal and solid-phase reaction process on the nanostructure, chemical stability and ion-exchange property of the ion-sieve material were examined with powder X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), N2 adsorption–desorption at 77K, and Li+ selective adsorption measurements. The lithium selective adsorption capacity was improved remarkably to 6.62mmolg−1 at equilibrium and about 5mmolg−1 at the initial lithium concentration of only 5.0mmoll−1, which is significant for lithium extraction from aqueous solutions with very low lithium content.