Lithium extraction/insertion process on cubic Li-Mn-O precursors with different Li/Mn ratio and morphology

Shu-Ying Sun,Xingfu Song,Qin-Hui Zhang,Jin Wang,Jian-Guo Yu

DOI: https://doi.org/10.1007/s10450-011-9356-0

2011-01-01

Abstract:The cubic phase LiMn 2 O 4 precursors are prepared by high-temperature calcinations (1003 K) of LiOH⋅H 2 O and MnO 2 mixture with Li/Mn molar ratio = 0.55. The Li 4 Mn 5 O 12 precursors are synthesized via low-temperature solid-phase reaction (673 K) of LiNO 3 and MnO 2 mixture with Li/Mn molar ratio = 1.0. The ion-sieves counterparts (named SMO-H and SMO-L, respectively) are obtained by the acid treatment of Li-Mn-O precursors. The structure, chemical stability, morphology, ion-exchange property and mechanism of Li-Mn-O precursors and MnO 2 ion-sieve were systematically examined via X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), selected-area electron diffraction (SAED), Infrared Spectroscopy (IR), X-ray photoelectron spectroscopy (XPS) and lithium ion selective adsorption measurements. The result shows the more compact Mn-O lattice makes the Li 4 Mn 5 O 12 spinel more stable after the Li + is extracted. The results of IR and XPS show adsorption process of SMO-H exists ion-exchange between the Li + and protons, and redox reaction, but only exists ion-exchange between the Li + and protons in SMO-L. Agglomeration is well-improved by low calcination temperature and the morphology of the Li 4 Mn 5 O 12 precursor and final MnO 2 ion-sieve are effectively controlled within low-dimensional structure. The maximum pH titration capacity of SMO-L for Li + is 6.76 mmol⋅g −1 , but only 3.47 mmol⋅g −1 for SMO-H. The ion-sieve obtained from Li 4 Mn 5 O 12 precursor is promising in the lithium extraction from brine or seawater.