Preparation and Lithium Adsorption Properties of Low-Dimensional Cubic Li4mn5o12 Nanostructure

Sun Shu-Ying,Zhang Qin-Hui,Yu Jian-Guo

DOI: https://doi.org/10.3724/sp.j.1077.2010.00626

IF: 1.292

2010-01-01

Journal of Inorganic Materials

Abstract:Pure beta-MnO2 oxide was synthesized by hydrothermal synthesis of MnSO4 center dot H2O and (NH4)(2)S2O8. Spinel-type Li4Mn5O12 precursors were synthesized via low temperature solid-phase reaction. Furthermore, MnO2 ion-sieves with Li+ selective adsorption property were prepared by the acid treatment process to completely extract Li+ from the spinel Li4Mn5O12 precursor. The effects of hydrothermal and solid-phase reaction process on the nanostructure, chemical stability and ion-exchange property of the ion-sieve material were examined with XRD, HRTEM, SAED, and Li+ selective adsorption measurements. The results show that Li4Mn5O12 precursor and final MnO2 ion-sieve are effectively controlled within low-dimensional structure, indicating that low temperature solid-phase reaction is more favorable to control the nanocrystalline structure than traditional high-temperature calcination process. The Li+ selective adsorption capacity is improved remarkably to 6.6 mmol/g at equilibrium and about 5.0 mmol/g at the initial Li+ concentration of only 5.0 mmol/L, which is significant for lithium extraction from aqueous solutions with very low lithium content.