Abstract:The conventional Ni-based IN738LC superalloy series are typically hardened by a fine distribution of closely spaced fine and coarse Ni 3 (Al, Ti)-type L1 2 ordered γ' precipitates, which is formed by solid-state nucleation and growth in the disordered γ matrix. However, outstanding high-temperature mechanical performance requires a high amount (∼9 wt%) of Co, which is the alloy's most expensive adding element. Here, we report a compositionally modified IN738LC alloy with a 50% reduction in Co content and a 20% increase in comparatively cheaper Mo content. This compositional modification caused more γ' precipitates with uniform distribution than those in the conventional counterpart subjected to the same heat treatments. The modified superalloy showed a twofold increase in high-temperature (750 °C) tensile elongation while maintaining the conventional one's strength (∼1.1 GPa) at the temperature. This remarkable ductility gain, while no loss in strength, was predominantly attributed to a transition in the high-temperature deformation mechanism, i.e., from multiple intersecting slip bands-indued stress localization for the conventional IN738LC alloy to unidirectional microtwins for the modified IN738LC material. More Mo and less Co contents could drive more coherent γ' precipitates in the annealed state and the high density of microtwins in the deformed state, resulting in stress delocalization and enhanced ductility at comparable strength. The findings of this study have significant implications for the development of cost-effective, strong, and ductile superalloys for high-temperature applications.

High Strength Nanocrystalline Ni-Co Alloy with Enhanced Tensile Ductility

Nano-precipitation strengthening regulated by nanotwins in CoCrNi alloy with super-high strength

Exceptional high-strain-rate tensile mechanical properties in a CrCoNi medium-entropy alloy

Enhanced Tensile Ductility in an Electrodeposited Nanocrystalline Ni

Enhancing Strength and Ductility of a Ni-26.6Co-18.4Cr-4.1Mo-2.3Al-0.3Ti-5.4Nb Alloy via Nanosized Precipitations, Stacking Faults, and Nanotwins

Tensile properties and deformation mechanisms of a new Ni–Co base superalloy from room temperature up to 750 °C

Achieving Excellent Strength-Ductility Balance in Single-Phase CoCrNiV Multi-Principal Element Alloy

Enhanced high-temperature ductility without strength drop in a lean Co Ni-based superalloy

Nanocrystallization Enabled Tensile Ductility of Co-Based Amorphous Microwires

Ductile–brittle–ductile Transition in an Electrodeposited 13 Nanometer Grain Sized Ni–8.6wt.% Co Alloy

Microstructure and properties of a novel ultra-high strength, high elasticity and high plasticity Cu–20Ni–20Mn-0.3Nb-0.3Cr-0.1Zr alloy

L1 2 nanoparticle-strengthened CoNi-based superalloy with ultrahigh yield stress developed using CALPHAD method

Microstructure and Tensile Properties of Al0.5CoCrCuFeNi Alloys Produced by Simple Rolling and Annealing

Enhancing strength-ductility synergy in a casting non-equiatomic NiCoCr-based high-entropy alloy by Al and Ti combination addition

Tensile Properties of a Non-Equiatomic Ni–Co–V Medium Entropy Alloy at Cryogenic Temperature

B2-strengthened Al-Co-Cr-Fe-Ni high entropy alloy with high ductility

Overcoming high-temperature strength-ductility trade-off by combination deformation twinning of C11b and D022 superlattices in a Ni-Cr-W/Mo-based superalloy

Nanodomained Nickel Unite Nanocrystal Strength with Coarse-Grain Ductility

Enhancing the strength-ductility trade-off in C 0.1 CrMnFeCoNi 0.8 high-entropy alloy: A combined experimental and DFT study

L12 nanoparticles-strengthened Co2Ni2Cr medium entropy alloy showing an outstanding tensile property

Breaking the trade-off between strength and ductility in nanostructured CrCoNi-based medium-entropy alloys by promoting twinning kinetics