Enhancing the strength-ductility trade-off in C 0.1 CrMnFeCoNi 0.8 high-entropy alloy: A combined experimental and DFT study

Sirui Huang,Hao Wu,Yujie Chen,Heguo Zhu

DOI: https://doi.org/10.1016/j.jmrt.2023.10.034

IF: 6.267

2023-10-06

Journal of Materials Research and Technology

Abstract:As a rapidly emerging class of metallic materials, high-entropy alloys (HEAs) provide the opportunity to develop novel alloys with superior mechanical properties through tackling the long-standing challenges, such as strength-ductility trade-off dilemma. Herein, C-doped CrMnFeCoNi 0.8 alloys were produced by vacuum induction melting. The addition of C up to 0.1 at % strengthens the CrMnFeCoNi 0.8 alloy without sacrificing ductility. Compared to the base alloy, the yield strength of the C 0.1 CrMnFeCoNi 0.8 alloy was increased by ∼40 % from 240.9 MPa to 334.2 MPa at no reduction in tensile ductility, mainly attributed to the formation of fully coherent carbide precipitates on the grain boundaries. The mechanical properties of the C 0.1 CrMnFeCoNi 0.8 alloy can be further enhanced by annealing. The alloy annealed at 950 °C exhibits a yield strength of 517.8 MPa, an ultimate tensile strength of 914.6 MPa, and an appreciable ductility (20.5 %), achieving an excellent combination of strength and ductility. Furthermore, the influence of C addition on the mechanical properties and electronic structures were explored using density functional theory (DFT) calculations to understand the enhanced strength-ductility synergy in the C 0.1 CrMnFeCoNi 0.8 alloy.

materials science, multidisciplinary,metallurgy & metallurgical engineering