Effect of rotary radius on the microstructures and shearing resistance of joint in com-stir friction stir spot welding

Fu Juan,Zhao Yong,Yan Keng,Zhang Nianqiang

DOI: https://doi.org/10.3969/j.issn.1673-4807.2011.05.004

2011-01-01

Abstract:The com-stir friction stir spot welding is adopted to make lap joints on the thin aluminum alloy board 2A12-T4 with a thickness of 2 mm.The joints are tested by shearing resistance at different rotary radii of com-stir FSSW.Fracture path and microstructure are observed and analyzed.Experimental results show that when other parameters remain constant and the rotary radius is 1.2 mm,the maximum shearing resistance of the joint can be realized and is 2 948 N.Moreover,as the rotary radius increases,the heat input increases.Macroscopic structure of stirred-zone widens and compacts,and shearing resistance increases,too.But large rotary radius may lead to large heat input,and it decreases the density of the macroscopic structure of stirred-zone.Also,holes and other defects occur,and the joint shearing resistance reduces.The metal flows intensively in the stirred zone that has some characteristics including minute grain size,compact structure and hard zones.