Microstructure and properties of friction stir welding 6061 aluminum alloy joint

Haiyan Wang,Wenjun Qi,Deng Nong,Feiyan Zheng

DOI: https://doi.org/10.3969/j.issn.0258-7076.2010.05.002

2010-01-01

Abstract:The 6061-T4 aluminum alloy plates with the thickness of 6 mm were welded by friction stir welding. Microstructure and fractographs of the friction stir welding (FSW) joint were studied and contrasted with base metal by optical microscope (OM) and scanning electron microscope (SEM). Meanwhile, the tensile properties and microhardness at room temperature were measured. According to the experimental results, the suited parameters of friction stir welding process for 6061-T4 aluminum alloy plate were selected as follows: the rotation speed of the mixing head was 1200 r · min-1, and the speed of the workpiece feeding during welding was 300 mm · min-1. The strength and toughness of the FSW joints were equal to or close to that of the base metal under the above parameters, which provided the alloys a dependable technology for applying to key components of autos. The microstructure and properties of the weld nugget zone in the FSW joint were significantly better than other areas. The heat affected zone was the weakest part in the joint. The weld nugget zone had the highest hardness while the heat affected zone had the lowest one. The grains were refined due to the recovery and recrystallization occurred in the metal of FSW joints. The fractograph analysis indicated that fracture occurred in the heat affected zone where the grains grew larger and the microstructure was coarsened for the rotation of the mixing head and the cumulating of heat quality. The optimization results of process parameters showed that there was a certain relationship between the influence of rotation speed and welding speed on joint properties. Adjustment of the processing parameters could control the microstructure of the heat affected zone effectively and improve the properties of the joint. Grain refining was the main reason for the improvement of the FSW joint's strength and toughness.