Abstract:In this study, we present a novel modified Stöber method utilizing cetyltrimethylammonium bromide (CTAB) as a mediator for the preparation of monodispersed, micron-sized supermicroporous silica particles. Observed results show prepared silica particles ranging in size from 0.64 to 1.36 μm with an increase in CTAB concentration from 1.0 to 5.0 mM. The particles exhibited low polydispersity (<5%), a high Brunauer-Emmett-Teller surface area (570 to 1064 m2/g), and pore volumes ranging from 0.22 to 0.39 cm3/g. The pore size, determined using the Barrett-Joyner-Halenda method from the adsorption branches of the isotherms, was approximately 1.9 nm, specifically 1.83, 1.85, and 1.90 nm, as the CTAB concentration increased from 1.0 to 2.5 and 5.0 mM, respectively. The resulting particles displayed a narrow distribution of pore diameters. In addition, to obtain an in-depth understanding of the role of CTAB on the preparation of silica particles, a possible mechanism is also investigated using conductivity, dynamic light scattering (DLS), zeta potential, FT-IR spectra, and transmission electron microscopy. Our findings demonstrate that CTAB plays multiple roles in the hydrolysis/condensation of TEOS (tetraethyl orthosilicate) and subsequent nucleation and growth of silica particles. CTAB acts as a template for superporosity, a stabilizer for colloids, and an accelerator for nucleation and growth, leading to formation of monodispersed micrometer silica particles. Further characterization through FT-IR and 29Si solid NMR spectra revealed that the micron silica particles were obtained with inhomogeneity in the condensation degree, allowing for selective etching through hot incubation to form micron-sized hollow silica spheres.

Preparation of Microsized Monodisperse Silica Spheres by Hydrolysis of Tetraethoxy Silane

Preparation of Monodisperse Silica Particles with Controllable Size and Shape

Fabrication of submicrosized monodisperse silica spheres using a continuing multi-step growth method

Monodisperse SiO2 Microspheres with Large Specific Surface Area: Preparation and Particle Size Control

Preparation of silica micro spheres via a semibatch sol–gel method

Preparation of silica microspheres by hydrolysis of silicon tetrachloride in microemulsion

Size-Controllable Synthesis of Worm-Like Sio2 Microspheres Using Dodecylamine As Direct Agent in Ethanol/Water Solvent System

Preparation of hollow mesoporous silica spheres by a sol–gel/emulsion approach

Synthesis of Mesoporous Silica Spheres by Using Neutral-cationic Surfactant and Semi-batch Growth

Micrometer‐sized Monodispersed Silica Spheres with Advanced Adsorption Properties

Preparation of Monodisperse Silica Mesoporous Microspheres with Narrow Pore Size Distribution

Novel and feasible method for synthesis of monodispersed hollow silicon dioxide submicrospheres

Microfluidic preparation of monodisperse polymeric microspheres coated with silica nanoparticles

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

One-step Synthesis of Highly Monodisperse Hybrid Silica Spheres in Aqueous Solution.

Synthesis of Ordered Mesoporous Silica Spheres with Controllable Diameter in Micrometer

A One-Step Ultrasonic Spray Pyrolysis Approach to Large-Scale Synthesis of Silica Microspheres

Preparation of Micrometer-Sized Mesoporous Silica Spheres Assisted by Methyl Cellulose

Impact of Varying the Concentration of Tetraethyl-OrthoSilicate on the Average Particle Diameter of Monodisperse Colloidal Silica Spheres

Monodispersed, Micron-Sized Supermicroporous Silica Particles by Cetyltrimethylammonium Bromide-Mediated Preparation

Controllable preparation and formation mechanism of monodispersed silica particles with binary sizes