Abstract:In this study, we present a novel modified Stöber method utilizing cetyltrimethylammonium bromide (CTAB) as a mediator for the preparation of monodispersed, micron-sized supermicroporous silica particles. Observed results show prepared silica particles ranging in size from 0.64 to 1.36 μm with an increase in CTAB concentration from 1.0 to 5.0 mM. The particles exhibited low polydispersity (<5%), a high Brunauer-Emmett-Teller surface area (570 to 1064 m2/g), and pore volumes ranging from 0.22 to 0.39 cm3/g. The pore size, determined using the Barrett-Joyner-Halenda method from the adsorption branches of the isotherms, was approximately 1.9 nm, specifically 1.83, 1.85, and 1.90 nm, as the CTAB concentration increased from 1.0 to 2.5 and 5.0 mM, respectively. The resulting particles displayed a narrow distribution of pore diameters. In addition, to obtain an in-depth understanding of the role of CTAB on the preparation of silica particles, a possible mechanism is also investigated using conductivity, dynamic light scattering (DLS), zeta potential, FT-IR spectra, and transmission electron microscopy. Our findings demonstrate that CTAB plays multiple roles in the hydrolysis/condensation of TEOS (tetraethyl orthosilicate) and subsequent nucleation and growth of silica particles. CTAB acts as a template for superporosity, a stabilizer for colloids, and an accelerator for nucleation and growth, leading to formation of monodispersed micrometer silica particles. Further characterization through FT-IR and 29Si solid NMR spectra revealed that the micron silica particles were obtained with inhomogeneity in the condensation degree, allowing for selective etching through hot incubation to form micron-sized hollow silica spheres.

Preparation of silica microspheres by hydrolysis of silicon tetrachloride in microemulsion

Controlled Formation of Silica Particles from Tetraethyl Orthosilicate in Nonionic Water-in-Oil Microemulsions

Preparation and Formation Mechanism of Silica Microcapsules (Hollow Sphere) by Water/Oil/Water Interfacial Reaction

Preparation of monodisperse nanosize silica-cadmium sulfide composites and hollow silica spheres in reverse micelle microemulsion

Preparation of hollow mesoporous silica spheres by a sol–gel/emulsion approach

Preparation of silica micro spheres via a semibatch sol–gel method

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

Monodispersed, Micron-Sized Supermicroporous Silica Particles by Cetyltrimethylammonium Bromide-Mediated Preparation

Preparation of Highly Monodisperse Hybrid Silica Nanospheres Using a One-Step Emulsion Reaction in Aqueous Solution

Preparation of hollow silica microspheres in W/O emulsions with polymers

Preparation of Micrometer-Sized Mesoporous Silica Spheres Assisted by Methyl Cellulose

Preparation of Monodisperse Silica Particles with Controllable Size and Shape

Using Hydrolysis of Silicon Tetrachloride to Prepare Highly Dispersed Precipitated Nanosilica

Preparation of silica microspheres with bimodal pore structure in micro-channel

Microdroplet-based Synthesis of Polymethylsilsesquioxane Microspheres with Controllable Size, Surface Morphology, and Internal Structure

Preparation of mesoporous submicrometer silica capsules via an interfacial sol-gel process in inverse miniemulsion.

Preparation of Highly Dispersed Precipitated Nanosilica in a Membrane Dispersion Microreactor

A novel low temperature vapor phase hydrolysis method for the production of nano-structured silica materials using silicon tetrachloride

Role of Hydrophobic Attraction and Hydrophobic Nanoconfined Channels in the Spray Drying Process for Synthesizing Hollow Microspheres from Silica Sol

Synthesis of Monodisperse Silica Microspheres with Solid Core and Mesopore Shell

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents