Abstract:In this study, we present a novel modified Stöber method utilizing cetyltrimethylammonium bromide (CTAB) as a mediator for the preparation of monodispersed, micron-sized supermicroporous silica particles. Observed results show prepared silica particles ranging in size from 0.64 to 1.36 μm with an increase in CTAB concentration from 1.0 to 5.0 mM. The particles exhibited low polydispersity (<5%), a high Brunauer-Emmett-Teller surface area (570 to 1064 m2/g), and pore volumes ranging from 0.22 to 0.39 cm3/g. The pore size, determined using the Barrett-Joyner-Halenda method from the adsorption branches of the isotherms, was approximately 1.9 nm, specifically 1.83, 1.85, and 1.90 nm, as the CTAB concentration increased from 1.0 to 2.5 and 5.0 mM, respectively. The resulting particles displayed a narrow distribution of pore diameters. In addition, to obtain an in-depth understanding of the role of CTAB on the preparation of silica particles, a possible mechanism is also investigated using conductivity, dynamic light scattering (DLS), zeta potential, FT-IR spectra, and transmission electron microscopy. Our findings demonstrate that CTAB plays multiple roles in the hydrolysis/condensation of TEOS (tetraethyl orthosilicate) and subsequent nucleation and growth of silica particles. CTAB acts as a template for superporosity, a stabilizer for colloids, and an accelerator for nucleation and growth, leading to formation of monodispersed micrometer silica particles. Further characterization through FT-IR and 29Si solid NMR spectra revealed that the micron silica particles were obtained with inhomogeneity in the condensation degree, allowing for selective etching through hot incubation to form micron-sized hollow silica spheres.

Preparation of Monodisperse Silica Particles with Controllable Size and Shape

Preparation of Microsized Monodisperse Silica Spheres by Hydrolysis of Tetraethoxy Silane

Controllable preparation and formation mechanism of monodispersed silica particles with binary sizes

A novel approach for the synthesis of monodispersed porous silica microspheres with high surface area

Preparation and formation mechanisms of monodispersed silicon dioxide spherical particles

Preparation of Monodisperse Nano-silica Microspheres

Systhesis of Monodispersed Silica Microspheres and the Formation Mechanism

Synthesis and formation mechanism of amorphous silica particles via sol–gel process with tetraethylorthosilicate

Preparation of Monodispersed Mesoporous Silica Spheres with Controllable Particle Size under an Alkaline Condition

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Synthesis and Characterization of Monodispersed Spherical Mesoporous Silica

Synthesis of Silica Particles with Precisely Tailored Diameter

Fabrication of submicrosized monodisperse silica spheres using a continuing multi-step growth method

Size-Controllable Synthesis of Worm-Like Sio2 Microspheres Using Dodecylamine As Direct Agent in Ethanol/Water Solvent System

Preparation of silica micro spheres via a semibatch sol–gel method

Monodisperse SiO2 Microspheres with Large Specific Surface Area: Preparation and Particle Size Control

Preparation of hollow mesoporous silica spheres by a sol–gel/emulsion approach

Synthesis of highly mono-dispersed mesoporous silica spheres

Synthesis of uniform-size hollow silica microspheres through interfacial polymerization in monodisperse water-in-oil droplets

Controlled synthesis of monodisperse silica particles

Monodispersed, Micron-Sized Supermicroporous Silica Particles by Cetyltrimethylammonium Bromide-Mediated Preparation