Influence of the Surface Electrical Property of Polymer Template Microspheres on the Morphology of Hollow Silica Microspheres
Guo-wei Duan,Li-zhao Xie,Chi Zhao,Mo-zhen Wang,Xue-wu Ge
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16257
2017-01-01
Acta Polymerica Sinica
Abstract:We prepared two kinds of monodispersed polystyrene (PS) microspheres with different surface electrical properties from the polymerization of styrene in water using different initiators. The PS microspheres prepared with potassium persulfate (KPS) as the initiator (PS-a) have negative zeta potential in water, and those prepared with 2,2'-azobis(2-methylpropionamidine) dihydrochloride (AIBA) as the initiator (PS-c) have positive zeta potential in water. Next, PS-a and PS-c microspheres were respectively used as the templates to prepare hollow SiO2 microspheres through a sol-gel process of tetraethoxysilane (TEOS) in an ethanol/ammonia medium. Based on the analysis on the products by FTIR, SEM, TEM, TGA, and N-2 adsorption-desorption isotherms, it was found that the distribution of OH- in the system depended on the surface electrical property of the PS template microspheres, which would lead to different formation processes of the silica shell on the template microspheres. When the PS-a microspheres were used as the template, the OH- ions were repulsed from the negative surface of the PS-a template microspheres, due to the electrostatic repulsion interaction. Thus, the SiO2 nanoparticles with a size of several tens of nanometers were firstly formed by hydrolysis and condensation of TEOS in the medium, and then adsorbed and packed on the surface of PS-a template microspheres through the polar interaction, resulting in the formation of a raspberry-like silica shell with macropores. After the PS-a template microspheres etched by toluene, the raspberry-like hollow silica microspheres were obtained. However, when PS-c template microspheres were used as the template, the OH- ions were adsorbed on the positive surface of the template microspheres. Then, a smooth and dense silica layer was grown directly from the surface of the template microspheres through the hydrolysis and the condensation of TEOS catalyzed by the adsorbed OH- ions. After calcination at 600 degrees C for 8 h, hollow silica microspheres with a smooth and mesoporous silica shell were produced. This work indicates that the morphology of the hollow silica microspheres can be controlled through the surface electrical property of the template microspheres. This study may lead to more applications of hollow silica microspheres in the area of control-release materials, drug carriers, and absorbents.