Abstract:The nanoindentation hardnesses of a commercially available soda-lime glass, a tetragonal ZrO2 polycrystalline and a hot-pressed Si3N4 were measured in the peak load range from 7.5 to 500 mN. The experimental results revealed that, for each material, the measured hardness exhibits a peak-load- dependence, i.e., indentation size effect (ISE). Such a peak-load-dependence was then analyzed using the Meyer’ law, the Hay–Kendall approach, the proportional specimen resistance (PSR) model, the elastic recovery model and the modified PSR model. The analyses revealed that: (1) Meyer's law provides a satisfactory description for the experimental data for each material but cannot provide any knowledge of the origin of the observed ISE; (2) the Hays–Kendall approach, the elastic recovery model and the PSR model yield meaningless values of the parameters included in the corresponding equations, invalidating the applicability of these models in analyzing the ISE in the nanoindentation region; (3) the modified PSR model is sufficient for describing the observed ISE but the physical meaning of this model seems to be more complex than those proposed originally. For each material, the true hardness was also determined based on the PSR model, the elastic recovery model and the modified PSR model, respectively. It was found that the true hardness values deduced based on different models are similar with each other and this similarity was attributed to the similarity between the empirical equations adopted in these models.

Analysis of the Indentation Size Effect on the Apparent Hardness for Ceramics

Examination of the Indentation Size Effect in Low-Load Vickers Hardness Testing of Ceramics

Effect of Microcracking on the Energy-Balance Relationship for Hardness Testing of Ceramics

On the description of indentation size effect in hardness testing for ceramics: Analysis of the nanoindentation data

Indentation toughness of ceramics: A modified approach

On the anstis equation used for the calculation of the indentation toughness for ceramics

The Effect of Indenter Angle on the Microindentation Hardness

Influence of Friction in Material Characterization in Microindentation Measurement.

Analysis of Load-Displacement Curves of Ceramics Measured with Low-Load Vickers Hardness Test: Indentation Size Effect

An energy-balance analysis for the size effect in low-load hardness testing

The Correlation Between Indentation Hardness and Material Properties with Considering Size Effect

Temperature-dependent Hardness Model of High-Temperature Materials Can Account for Indentation Size Effect

Indentation hardness of mullite based ceramics

Assessing the Elastic Parameters and Energy-Dissipation Capacity of Solid Materials: A Residual Indent May Tell All

Effect of Load-Dependence of Hardness on Indentation Toughness Determination for Soda-Lime Glass

Meyer analysis of the indentation size effect in the low-load hardness of (Ce,Y)-TZP/Al2O3 composites

The Mechanics of Indentation Induced Lateral Cracking

Study on Size Effect in Indentation Tests

Apparent indentation size effect of EB-PVD thermal barrier coatings

Theoretical Analysis of the Relationships Between Hardness, Elastic Modulus, and the Work of Indentation for Work-Hardening Materials

Examining the Effect of Pileup on the Accuracy of Sharp Indentation Testing