Abstract:A new type of non-oxide sintering additive of YH2 was introduced for the fabrication of AlN ceramics with high thermal conductivity and flexural strength. The effects of YH2 addition (0–5 wt%) on the phase composition, densification, microstructure, thermal conductivity and flexural strength of pressureless sintered AlN ceramics were investigated and compared with those Y2O3-added samples (1–5 wt%). The addition of 1 wt% YH2 led to an in-situ reduction reaction with oxygen impurities, the formation of Y2O3 and finally the formation of yttrium aluminate, which in turn improved densification and microstructure. A high flexural strength (408.69 ± 28.23 MPa) was achieved. The addition of 3 wt% YH2 increased the average grain size and purified the lattice. All these effects are believed to help achieve a high thermal conductivity of 184.82 ± 1.75 W·m−1·K−1. Although the thermal conductivity was close to the value of 3 wt% Y2O3-added sample, its strength was much increased to 381.53 ± 43.41 MPa. Meanwhile, it demonstrated a good combination of the thermal conductivity and flexural strength than the values reported in some literature. However, further increasing the YH2 addition to 5 wt% resulted in a high N/O ratio that inhibited the densification behavior of AlN ceramics. The current study showed that AlN ceramics with excellent thermal and mechanical properties could be obtained by the introduction of a suitable YH2 additive.

Effect of Adding Method of Sintering Additive on Mechanical Properties of AIN Ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Microstructure and Mechanical Properties of Aln Ceramics Sintered with Yttrium Nitrate

Effects of sintering additives on mechanical properties and microstructure of Si3N4 ceramics by microwave sintering

Effect of Additive Sm2O3 on Synthesizing AlN Ceramics at High Pressure

Effect of Different Sintering Additives on the Microstructure, Phase Compositions and Mechanical Properties of Si3N4/SiC Ceramics

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Effect of additions on the properties of Al2O3/BN machinable ceramics

Effects of Y2O3-LaF3 on the Low Temperature Sintering and Thermal Conductivity of AlN Ceramics

Effect of Sintering Additive Composition on Microstructure and Mechanical Properties of Silicon Nitride

Effects of MgAl2O4-ZrO2 Addition on Sintering Behaviors and Mechanical Properties of Silicon Nitride Ceramics

Effect of a New Additive on Mechanical Properties of Hot-Pressed Silicon Carbide Ceramics

Effect of Different Sintering Additives on the Reaction-Bonded Si3N4/SiC Composite Ceramics

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

Effect of Composite Sintering Additives Containing Non-Oxide on Mechanical, Thermal and Dielectric Properties of Silicon Nitride Ceramics Substrate

Effects of YH2 addition on pressureless sintered AlN ceramics

Effect of composite sintering aids system on properties of pressureless sintered AlN ceramics

Effect of additive content on the microstructure and room‐temperature and high‐temperature mechanical properties of Si3N4 ceramics

Influence of Yttria–Alumina Content on Sintering Behavior and Microstructure of Silicon Nitride Ceramics

Effect of Sintering Additives on Microstructure and Mechanical Properties of Porous Silicon Nitride Ceramics