Abstract:Thermal, mechanical and tribological properties of carbon fabric/resin laminated composites containing carbon fiber powder with different densities. Carbon fabric/resin laminated composites (CFRC) are extensively used in aerospace, transportation, and other fields owing to their superiorities of lightweight, high strength, and convenient integral molding. Therefore, strong interlaminar binding and prominent wear resistance are urgent requirements for avoiding premature failure of laminated materials in harsh working environments. To elevate the superficial wear resistance and interlaminar bonding strength of composites simultaneously, the modified composites were obtained by introducing carbon fiber powder (CFP) with different densities on the surface of the composites and between layers. The experimental results indicate that CFP can be evenly distributed in the interlaminar resin enrichment zone of the sample (CFRC‐40) when the deposition density is 40 g/m2. Consequently, CFRC‐40 presents optimal thermal conductivity owing to better heat transfer bridges between layers of the composite established by CFP. At the same time, the mechanical properties such as the tensile, impact, and interlaminar shear strengths of CFRC‐40 are improved by 42.8%, 10.2%, and 8.5%, respectively, compared with the original CFRC, which are attributed to the absorption of crack propagation energy and the inhibition of crack propagation by CFP. Furthermore, the dynamic friction coefficient maintains at a high level after introducing CFP with a density of 40 g/m2, while the wear rate significantly decreases by 61.2% from 12.99 × 10−14 m3(N m)−1 to 5.04 × 10−14 m3(N m)−1. This study proposes an innovative strategy to improve the interlaminar bonding of carbon fabric/resin laminated composite, which is conducive to obtaining composite with excellent mechanical and tribological properties. Highlights A facile and effectual method was adopted to introduce carbon fiber powder (CFP) into the interlamination and surface of the composites simultaneously. The mechanical properties and abrasive resistance of the composites were obviously strengthened by regulating the content and distribution of CFP. CFP at a certain scale, could not only hinder the propagation of cracks but also alleviate the surface wear and extend the service life of composites.

Microstructure and mechanical properties of carbon foams and fibers reinforced carbon composites densified by CLVI and pitch impregnation

Microstructure and mechanical properties of carbon graphite composites reinforced by carbon nanofibers

Improving carbon/carbon composites mechanical and thermal properties by the co‐carbonization of pre‐oxidized carbon fiber and pitch

Mechanical and thermal conduction properties of carbon/carbon composites with different carbon matrix microstructures

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Analysis of transverse thermal conductivity for mesophase pitch-based carbon fibers and the through-thickness heat conduction of their composites

Enhanced mechanical and damping properties of carbon fiber/epoxy composites by introducing the microcapsule particles

Modification of isotropic pitch by tailoring chemical structure and fraction contents for enhancing carbon fiber mechanical properties

Effect of oxygen-introduced pitch precursor on the properties and structure evolution of isotropic pitch-based fibers during carbonization and graphitization

Preparation and characterization of carbon felt/carbon composites by chemical vapor infiltration process

Effect of microstructure evaluation during the PIP process on macroscopic properties of C/C composites

Effect of Fiber Mass Fraction on Microstructure and Properties of 2D CF-GO/EP Composite Prepared by VIHPS

Preparation of fixed length carbon fiber reinforced plastic composite sheets with isotropic mechanical properties

Preparation, microstructure and properties of three-dimensional carbon/carbon composites withhigh thermal conductivity

LIQUID IMPREGNATION METHOD USED TO DENSITY C/C COMPOSITES

Effect of carbon fiber reinforcement on the compressive and thermal properties of hollow glass microspheres/epoxy syntactic foam

Influences of Fiber Volume Content on the Mechanical Properties of 2D Plain Carbon-Fiber Woven Composite Materials

Preparation and thermal conduction property of expanded graphite matrix composites

EFFECT OF CARBON NANOFIBERS ADDITION ON DENSIFICATION AND MECHANICAL PROPERTIES OF CARBON/CARBON COMPOSITES

Improving mechanical and tribological properties of carbon fabric/resin laminated composites by carbon fiber powder

Unveiling the microcrystal structure evolution of carbon fibers induced by thermal soaking of mesophase pitch