Abstract:Effective mechanochemically-aided recycling of cobalt from the cathode of Lithium-ion batteries was achieved via a planetary ball mill with sulfuric acid and hydrogen peroxide system. By applying single factor experiments and response surface methodology (RSM), the optimal solution of the maximum leaching rate of cobalt was realized. The optimal conditions determined were H 2 SO 4 concentration of 0.5 mol/L, H 2 O 2 concentration of 2 mol/L, ball-to-powder mass ratio of 35:1, solid-to-liquid ratio of 20 g/L, reaction time of 120 min, revolution speed of 100 r/min, rotation speed of 468 r/min. Under these conditions, leaching efficiency of cobalt achieved 98.96%. Additionally, the importance of each factor was experimentally quantified, and the order of their influence was reaction time > rotation speed > revolution speed by RSM statical analysis. It was experimentally verified that the used mechanochemical-aided method was well suited for leaching of cobalt from spent LIBs. Mechanism analysis exhibits that the layered structure of the LiCoO 2 crystals collapsed under the destructive action of mechanical forces, Co 3+ in LiCoO 2 crystals is reduced to Co 2+ by H 2 O 2 . At the same time, the chemical bonds of Co(II)–O and Li–O are destroyed under the action of sulfuric acid to release Co 2+ and Li + . In the process of cobalt recovery, CoC 2 O 4 and CoC 2 O 4 4H 2 O were obtained with oxalic acid as precipitation, and the precipitate were completely converted into Co 3 O 4 after calcination. This process can present a highly efficient and feasible approach for the reuse of metals from the cathode of spent Li-ion batteries.

Leaching cobalt from spent Li-ion battery by sulfuric acid-hydrogen peroxide

Removal of impurity metals as phosphates from Lithium-ion battery leachates

Succinic Acid-Based Leaching System: A Sustainable Process for Recovery of Valuable Metals from Spent Li-ion Batteries

Mechanochemically-aided leaching of cobalt from the cathode of spent Lithium-ion batteries

A combined process for cobalt recovering and cathode material regeneration from spent LiCoO2 batteries: Process optimization and kinetics aspects

Recovery of Li and Co in Waste Lithium Cobalt Oxide-Based Battery Using H1.6Mn1.6O4

Extraction of Co and Li2CO3 from cathode materials of spent lithium-ion batteries through a combined acid-leaching and electro-deoxidation approach

Separation of cobalt and lithium from spent lithium-ion battery leach liquors by ionic liquid extraction using Cyphos IL-101

Effective leaching of spent lithium-ion batteries using DL-lactic acid as lixiviant and selective separation of metals through precipitation and solvent extraction

Recycling of Valuable Metals from the Priority Lithium Extraction Residue Obtained through Hydrogen Reduction of Spent Lithium Batteries

Kinetics of Ni and Co Recovery via Oxygen-Enriched Pressure Leaching from Waste Lithium-Ion Batteries

Hydrometallurgical Process Of Waste Cathodic Materials From Lithium Ion Battery Plants

Extraction of Valuable Metals from Waste Battery Material

Study of Spent Battery Material Leaching Process

Efficient recovery of lithium as Li2CO3 and cobalt as Co3O4 from spent lithium-ion batteries after leaching with p-toluene sulfonic acid

Ascorbic-acid-assisted Recovery of Cobalt and Lithium from Spent Li-ion Batteries

Coupling Electrochemical Leaching with Solvent Extraction for Recycling Spent Lithium-Ion Batteries

Leaching Behavior Analysis of Valuable Metals from Lithium-Ion Batteries Cathode Material

Selective recovery of lithium from spent lithium iron phosphate batteries using oxidation pressure sulfuric acid leaching system

A Combined Recovery Process Of Metals In Spent Lithium-Ion Batteries

Recovery of critical metals from spent Li-ion batteries: Sequential leaching, precipitation, and cobalt–nickel separation using Cyphos IL104