Abstract:In the present manuscript, a simple hydrometallurgy process for recovering and recycling cobalt from spent lithium cobalt oxide LiCoO2 (LCO) in lithium-ion batteries (LIBs) is described. First, the black material (BM) containing LCO active material is extracted by discharging, dismantling and detachment of cathode active materials with an organic solvent. Then, sulfuric acid (H2SO4) and hydrogen peroxide (H2O2) are used to fully dissolve Co and Li in an aqueous solution at high dissolution efficiency (more than 99% of Li and Co). After a purification step, Co is selectively precipitated and separated from Li, as CoCO3, using a simple method. Results show that the obtained CoCO3 crystals have a unique sheets-like structure with a purity of more than 97% and could be reused to regenerate LCO active material for LIB. The as-prepared sheet-like CoCO3 was then converted to flower-like LCO through a solid-state reaction with commercial lithium carbonate (Li2CO3). Electrochemical performances of the regenerated LCO (LCOReg) in LIB have been studied. Interestingly, the flower-like LCOReg showed a good charge capacity of about 145 mAh.g−1 at the first cycle, compared to LCO synthesized from commercial cobalt and lithium precursors (LCOCom). Specific charge capacity and columbic efficiency also remained relatively stable after 60 charge/discharge cycles. The proposed recycling process of Co in the present work doesn’t require the use of the complicated and expensive solvent extraction method and thus it is simple, cost-effective, environmentally-friendly and could be used for recovering high purity critical metals such as Co and Li from spent LIBs at the industrial scale.

Mechanochemically-aided leaching of cobalt from the cathode of spent Lithium-ion batteries

Enhancement of leaching of cobalt and lithium from spent lithium-ion batteries by mechanochemical process

Recover Lithium and Prepare Nano-Cobalt from Spent Lithium Ion Batteries Using a One-Pot Mechanochemical Reaction

Ascorbic-acid-assisted Recovery of Cobalt and Lithium from Spent Li-ion Batteries

Eco-Friendly Organic Acid-Assisted Mechanochemical Process for Metal Extraction from Spent Lithium-Ion Batteries

Recovery of cobalt from spent lithium ion batteries using sulphuric acid leaching followed by solid–liquid separation and solvent extraction

Converting spent lithium cobalt oxide battery cathode materials into high-value products via a mechanochemical extraction and thermal reduction route

Succinic Acid-Based Leaching System: A Sustainable Process for Recovery of Valuable Metals from Spent Li-ion Batteries

Recycling for Recovery of Critical Metals from LiCoO2 Cathode Material Through Methanesulfonic Acid-Citric Acid Organic Leaching System

A mechanochemical method for one-step leaching of metals from spent LIBs

Novel Approach to Recover Cobalt and Lithium from Spent Lithium-Ion Battery Using Oxalic Acid.

A combined process for cobalt recovering and cathode material regeneration from spent LiCoO2 batteries: Process optimization and kinetics aspects

Extraction of Co and Li2CO3 from cathode materials of spent lithium-ion batteries through a combined acid-leaching and electro-deoxidation approach

Leaching Process for the Recovery of Valuable Metals from Spent Lithium-nickel-cobalt-manganese-oxide-based Lithium-ion Batteries

Recovery of Li, Ni, Co and Mn from spent lithium-ion batteries assisted by organic acids: Process optimization and leaching mechanism

Efficient extraction of valuable metals from spent LiNi0.5Co0.2Mn0.3O2 cathode based on an acid-free leaching process

Highly Selective Extraction of Lithium from Spent NCM Cathode Powder Reconstructive Electrode by Acid-Free Electrochemical Process

Mechanochemically assisted persulfate activation for the facile recovery of metals from spent lithium ion batteries

Leaching Process for Recovering Valuable Metals from the LiNi1/3Co1/3Mn1/3O2 Cathode of Lithium-Ion Batteries.

Synthesis and Recyclability of Sheet-like Cobalt Carbonate Recovered from Spent Li-Ion Batteries Using a Simple Hydrometallurgy Process

Mechanochemical upcycling of spent LiCoO2 to new LiNi0.80Co0.15Al0.05O2 battery: An atom economy strategy