Strengthening Valuable Metal Recovery from Spent Lithium-Ion Batteries by Environmentally Friendly Reductive Thermal Treatment and Electrochemical Leaching
Shuya Lei,Yintao Zhang,Shaole Song,Rui Xu,Wei Sun,Shengming Xu,Yue Yang
DOI: https://doi.org/10.1021/acssuschemeng.1c00937
2021-04-21
Abstract:The traditional acid leaching method for recycling valuable metals from the cathode material of spent lithium-ion batteries (LIBs) has encountered the problems of high consumption of H<sub>2</sub>SO<sub>4</sub> and reducing agents. In this study, a novel process has been developed to strengthen valuable metal recovery from spent lithium-ion batteries by reductive thermal treatment and electrochemical leaching. With the help of reductive thermal treatment under the conditions of <i>R</i> = 1600 °C and 120 min, the layered structure of the cathode material LiNi<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>O<sub>2</sub> is reduced to a mixture of Li<sub>2</sub>CO<sub>3</sub>, NiO, Co<sub>3</sub>O<sub>4</sub>, Mn<sub>2</sub>O<sub>3</sub>, and MnO<sub>2</sub> due to the oxygen releasing from the framework. The destruction of the layered crystal structure reduces the difficulty of leaching valuable metals. 90.59% Ni, 90.53% Co, 66.40% Mn, and 100% Li were leached under the optimal conditions of 20 mL/g liquid–solid ratio, 1.5 M H<sub>2</sub>SO<sub>4</sub>, 0.8 A, and 150 min at room temperature. Comparing the processes of reductive thermal treatment with acid leaching and direct electrochemical leaching of spent cathode material under the same leaching conditions, the proposed approach can achieve the highest metal recovery and economic benefits. It can be implemented at room temperature, decreases the application of reducing agent and sulfuric acid, and makes full use of spent graphite, resulting in a greener recycling process for recovering valuable metals from spent LIBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c00937?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c00937</a>.XRD pattern of spent cathode materials, the picture of roasted product under conditions of <i>R</i> = 1, at 600 °C for 180 min, XPS of Ni, Co, and Mn for the electrochemical residues under conditions of 1.5 M H<sub>2</sub>SO<sub>4</sub>, 0.8 A for 150 min, the composition of spent cathode materials, calculation of the cost, benefit, and profit, and comparison of leaching valuable metals by proposed and existing methods (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c00937/suppl_file/sc1c00937_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology