Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Effects of Alkalinity on the Hydrothermal Synthesis of Lead Titanate Nanotube Arrays

Effect of Alkalinity on the Hydrothermal Synthesis of Li2zro3 Nanotube Arrays

Effects of Hydrothermal Time on the Morphologies of Rutile TiO2 Hierarchical Nanoarrays and Their Optical and Photocatalytic Properties

Hydrothermal Synthesis and Phase-, Morphology-Evolution Mechanism of Lead Titanate Nanostructures Assisted with Tetramethylammonium Hydroxide

Synthesis and Growth Mechanism of Lead Titanate Nanotube Arrays by Hydrothermal Method

Hydrothermal Synthesis and Characterization of Single-Crystal Lead Titanate Nanoflakes

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Hydrothermal Synthesis and Photoluminescence of Pre-Perovskite Lead Titanate Nanofibers

Effect of NaOH Concentration on Formation of Ba4Ti13O30 and BaTi5O11 Nanocrystals Prepared by Hydrothermal Method

Effect of KOH Concentration on the Phase and Morphology of Hydrothermally Synthesized Pb0.70La0.30TiO3 Fine Powders

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Effects of pH on Preparation and Properties of CaTi<sub>2</sub>O<sub>4</sub>(OH)<sub>2</sub> by Hydrothermal Method

Low Temperature Hydrothermal Synthesis and Performances of Nanotube Patterned Barium Titanates Thin Films

Photocatalytic activity of PbTiO<sub>3</sub> nanocrystals synthesized by hydrothermal method

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Hydrothermal Synthesis Of Thin Films Of Barium Titanate Nanotube Arrays

Hydrothermal Synthesis of Aluminum Oxy-Hydroxide Nanorod and Nanotube Arrays

Hierarchical Titanate Nanostructures Through Hydrothermal Treatment of Commercial Titania Powders

Effects of Synthesis Parameters on Controllable Growth of Highly-Ordered TiO2 Nanotube Arrays

Oriented nanostructured titanates array from low concentration alkaline solution via hydrothermal process.